Temperature evolution, microstructure and mechanical properties of friction stir welded thick 2219-O aluminum alloy joints
AbstractThe aim of this work is to investigate the temperature evolution, microstructure and mechanical properties of the joint during friction stir welding of thick 2219-O aluminum alloy with the butt joint. Different types of thermocouple layouts were designed to measure the temperature evolutions during tool inserting and stable welding processes. Dynamic recrystallised structures in the weld nugget zone (WNZ) were observed and different grain sizes were presented through the thickness. Tensile testing results indicated that the tensile strength (σb) and yield strength (σ0.2) of joints increased and the elongation (δ) of joints decreased with increasing the tool rotary speed. The joint top had the highest mechanical properties. Most of the failures presented a ductile fracture in the joints. Vickers microhardness was measured across the joint top, middle and bottom, and through the thickness in the WNZ. The result showed that the microhardness of different zones varied significantly.
Temperature evolution, microstructure and mechanical properties of friction stir welded thick 2219-O aluminum alloy joints
AbstractThe aim of this work is to investigate the temperature evolution, microstructure and mechanical properties of the joint during friction stir welding of thick 2219-O aluminum alloy with the butt joint. Different types of thermocouple layouts were designed to measure the temperature evolutions during tool inserting and stable welding processes. Dynamic recrystallised structures in the weld nugget zone (WNZ) were observed and different grain sizes were presented through the thickness. Tensile testing results indicated that the tensile strength (σb) and yield strength (σ0.2) of joints increased and the elongation (δ) of joints decreased with increasing the tool rotary speed. The joint top had the highest mechanical properties. Most of the failures presented a ductile fracture in the joints. Vickers microhardness was measured across the joint top, middle and bottom, and through the thickness in the WNZ. The result showed that the microhardness of different zones varied significantly.
Temperature evolution, microstructure and mechanical properties of friction stir welded thick 2219-O aluminum alloy joints
Xu, Weifeng (author) / Liu, Jinhe (author) / Luan, Guohong (author) / Dong, Chunlin (author)
2008-09-10
8 pages
Article (Journal)
Electronic Resource
English
| British Library Online Contents | 2009
Microstructure and mechanical properties of friction stir welded joints in 2219-T6 aluminum alloy
| British Library Online Contents | 2009
| British Library Online Contents | 2009
Mechanical and corrosion properties of friction stir welded joints of Al-Cu alloy 2219-T87
| British Library Online Contents | 2015