Prediction of the critical conditions for initiation of dynamic recrystallization
AbstractBoth the critical stress and strain for initiation of dynamic recrystallization (DRX) were determined using: (1) the strain hardening rate versus stress curve, (2) the natural logarithm of strain hardening rate versus strain curve, and (3) the constitutive equations. In order to perform these analyses, the behavior of a 17-4 PH stainless steel during hot compression test was investigated at temperatures of 950–1150°C and strain rates of 0.001–10s−1. The first and second methods were found to be the best ones for determining the critical stress and strain, respectively. The Cingara constitutive equation was also used to model the flow curves up to the peak point and subsequently was used for predicting the critical strain. In summary, for 17-4 PH stainless steel, the DRX was found to start when the normalized stress and strain reach to the values of 0.89 and 0.47, respectively.
Prediction of the critical conditions for initiation of dynamic recrystallization
AbstractBoth the critical stress and strain for initiation of dynamic recrystallization (DRX) were determined using: (1) the strain hardening rate versus stress curve, (2) the natural logarithm of strain hardening rate versus strain curve, and (3) the constitutive equations. In order to perform these analyses, the behavior of a 17-4 PH stainless steel during hot compression test was investigated at temperatures of 950–1150°C and strain rates of 0.001–10s−1. The first and second methods were found to be the best ones for determining the critical stress and strain, respectively. The Cingara constitutive equation was also used to model the flow curves up to the peak point and subsequently was used for predicting the critical strain. In summary, for 17-4 PH stainless steel, the DRX was found to start when the normalized stress and strain reach to the values of 0.89 and 0.47, respectively.
Prediction of the critical conditions for initiation of dynamic recrystallization
Mirzadeh, H. (author) / Najafizadeh, A. (author)
2009-09-19
6 pages
Article (Journal)
Electronic Resource
English
Prediction of the critical conditions for initiation of dynamic recrystallization
| British Library Online Contents | 2010
Determination of critical strain for initiation of dynamic recrystallization
| British Library Online Contents | 2010
| British Library Online Contents | 2011
Prediction of the critical conditions for dynamic recrystallization in the austenitic steel 800H
| British Library Online Contents | 2004