Hot deformation behavior and microstructural evolution of Ag-containing 2519 aluminum alloy
AbstractThe hot deformation behaviors of Ag-containing 2519 aluminum alloy were studied by isothermal compression at 300–500°C with strain rates from 0.01s−1 to 10s−1. The microstructural evolution of the alloy was investigated using Polyvar-MET optical microscope and Tecnai G2 20 transmission electron microscope (TEM). It has been shown that the flow stress of the alloy increases with increasing the strain rate and decreasing the deformation temperature. When the strain rate is lower than 10s−1, the flow stress increases with increasing strain until the stress reached the peak value, after which the flow stress remains almost constant. This result indicates that dynamic recovery happens during deformation. When the strain rate is 10s−1 and the temperature is higher than 300°C, serrated flow behavior is generally observed with the stress decreasing with increasing strain, a typical phenomenon of dynamic recrystallization.
Hot deformation behavior and microstructural evolution of Ag-containing 2519 aluminum alloy
AbstractThe hot deformation behaviors of Ag-containing 2519 aluminum alloy were studied by isothermal compression at 300–500°C with strain rates from 0.01s−1 to 10s−1. The microstructural evolution of the alloy was investigated using Polyvar-MET optical microscope and Tecnai G2 20 transmission electron microscope (TEM). It has been shown that the flow stress of the alloy increases with increasing the strain rate and decreasing the deformation temperature. When the strain rate is lower than 10s−1, the flow stress increases with increasing strain until the stress reached the peak value, after which the flow stress remains almost constant. This result indicates that dynamic recovery happens during deformation. When the strain rate is 10s−1 and the temperature is higher than 300°C, serrated flow behavior is generally observed with the stress decreasing with increasing strain, a typical phenomenon of dynamic recrystallization.
Hot deformation behavior and microstructural evolution of Ag-containing 2519 aluminum alloy
Li, Huizhong (author) / Li, Zhou (author) / Song, Min (author) / Liang, Xiaopeng (author) / Guo, Feifei (author)
2009-10-30
6 pages
Article (Journal)
Electronic Resource
English
Hot deformation behavior and microstructural evolution of Ag-containing 2519 aluminum alloy
| British Library Online Contents | 2010
Aluminum Alloy 2519 in Military Vehicles
| British Library Online Contents | 2002
Hot Deformation Behavior of 2519 Al Alloy during Isothermal Compression
| British Library Online Contents | 2007
Effect of pre-deformation on the stress corrosion cracking susceptibility of aluminum alloy 2519
| British Library Online Contents | 2007
Effect of Cold Plastic Deformation on Mechanical Properties of Aluminum Alloy 2519 After Ageing
| British Library Online Contents | 2014