Properties of alite cements

Mehta, P.K. / Pirtz, D. / Polivka, M.

AbstractFor carrying out a comprehensive investigation on physical and mechanical properties of alite mortars and concretes, large quantities of monoclinic alite were produced at the University of California at Berkeley. Laboratory-size specimens were employed to determine strength, drying shrinkage, and sulfate resisting characteristics of mortars and concretes made with alite cements. Small amounts of gypsum (3%) addition accelerated the setting and hardening of the alite cements, however, large amounts (6%) resulted in strength deterioration. Drying shrinkage of alite concretes was significantly lower than portland cement concretes of the same fineness. Long term sulfate immersion of concrete specimens made with an alite cement caused serious spalling and strength loss.

ZusammenfassungAn der Universitat von California in Berkeley wurden intensive Untersuchugen über das physikaliscke und mechanische Verhalten von Alitmörtel und Alitbeton durchgeführt. Da die bei Standard untersuchungen üblichen Probenabmessungen verwendet wurden, mussten grosse Mengen von Monclinic-Alit hergestellt wurden. An den mit Alit erstallten Proben ars Mörtel und Beton wurden in Versuchreiben das Festigkeitsverhalten, das Schwinden und der Widerstand gegen Sulfateinwirking untersucht.So beschleunigte die Zugabe von geringen Gipsanteilen (3%) das Erstarren und die Erhärtung dur Alitzement, während grossore Gipsanteile (6%) zu einer Festigkeiteabrahme führten. Das Schwinden von Alitbeton war dentlich geringer als das bu einem Beton der mit portland zement der selben Feinheit hergeställt worden war. Die Langzeiteinwirkung von sulfaten anf Betonproben mit Alitzement erzeugte Absprengungen und einen signifikanten Abbau der Festigkeit.