Investigation on the corrosion behavior of aluminum alloys 3A21 and 7A09 in chloride aqueous solution
Highlights 3A21 alloy had good corrosion resistance due to its uniform and finemicrostructure. The serious pitting corrosion of 7A09 was owing to its microstructural heterogeneity. The anodic activity of the intermetallics of 7A09 ceased after immersion for 4days.The corrosion products were mainly composed of Al2O3, Al(OH)3 and AlCl3.
Abstract The corrosion behavior of aluminum alloys 3A21 and 7A09 in 3.5%NaCl solution were studied by using microstructure examination, electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and Fourier transform-infrared (FT-IR) spectroscopy. Results show that the two kinds of alloys both suffer from pitting corrosion and the corrosion of 7A09 is much more serious than that of 3A21. The EIS tests reveal high corrosion rate for 7A09 alloy and good corrosion resistance for 3A21 alloy. XPS and FT-IR analysis demonstrate that the corrosion products are mainly composed of Al2O3, Al(OH)3 and AlCl3.
Investigation on the corrosion behavior of aluminum alloys 3A21 and 7A09 in chloride aqueous solution
Highlights 3A21 alloy had good corrosion resistance due to its uniform and finemicrostructure. The serious pitting corrosion of 7A09 was owing to its microstructural heterogeneity. The anodic activity of the intermetallics of 7A09 ceased after immersion for 4days.The corrosion products were mainly composed of Al2O3, Al(OH)3 and AlCl3.
Abstract The corrosion behavior of aluminum alloys 3A21 and 7A09 in 3.5%NaCl solution were studied by using microstructure examination, electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and Fourier transform-infrared (FT-IR) spectroscopy. Results show that the two kinds of alloys both suffer from pitting corrosion and the corrosion of 7A09 is much more serious than that of 3A21. The EIS tests reveal high corrosion rate for 7A09 alloy and good corrosion resistance for 3A21 alloy. XPS and FT-IR analysis demonstrate that the corrosion products are mainly composed of Al2O3, Al(OH)3 and AlCl3.
Investigation on the corrosion behavior of aluminum alloys 3A21 and 7A09 in chloride aqueous solution
Wang, Bin (author) / Zhang, Lunwu (author) / Su, Yan (author) / Mou, Xianliang (author) / Xiao, Yong (author) / Liu, Jie (author)
2013-02-27
7 pages
Article (Journal)
Electronic Resource
English
| British Library Online Contents | 2013
Corrosion Behavior of 3A21 Aluminum Alloy in Ethylene Glycol-water Solution
| British Library Online Contents | 2014
Effect of Organosilane Coatings on Corrosion Resistance of 3A21 Aluminum Alloy
| British Library Online Contents | 2011
| British Library Online Contents | 2015
Numerical Analysis on Precision Forging of 7A09 Aluminum Impeller
| British Library Online Contents | 2009