Expansion associated with ettringite formation at different temperatures

Negro, A. / Bachiorrini, A.

AbstractExpansion of hydrated mixtures made with C3A, CaSO4 · 2H2O, Ca(OH)2 and SiO2, at 22, 30, 40, 50, 60°C, was studied to verify if expansion is associated with colloidal ettringite formation or with the solid state conversion of C4AH13 to monosulfate hydrate in presence of calcium hydroxide. From the results of our investigation it can be drawn the conclusion that mortars expansion is in connection with colloidal ettringite formation and the monosulfate hydrate is formed only when the greatest expansion is ended. The increase in hydration temperature seem to be favorable to the formation of colloidal ettringite.

ResumenL'espansione a seguito d'idratazione di malte constituite da C3A, CaSO4 · 2H2, Ca(OH) e SiO2 condotta a temperature di 22, 30, 40, 50, 60°C è stata eseguita per verificare se l'effetto espansivo fosse associabile alla formazione di ettringite colloidale o alla conversione allo stato solido del C4AH13 in monosolfoalluminato idrato in presenza di idrossido di calcio. I risultati ottenuti mostrano che l'espansione delle malte è dovuta alla formazione di ettringite colloidale mentre il monosolfoalluminato idrato si forma solo quando la fase di massima espansione del sistema è superata. L'incremento della temperatura d'idratazione sembra favorire inizialmente la formazione di ettringite colloidale.