Effect of prolonged drying upon the silicate structure of hydrated alite pastes: Fid-Bau Portal

Effect of prolonged drying upon the silicate structure of hydrated alite pastes

Parrott, L.J. / Young, J.F.

AbstractThe effects of prolonged drying and initial water/alite ratio upon the silicate structure of hydrated alite paste were examined using quantitative gel permeation chromatography of the trimethylsilyl silicate derivatives. The effects of drying and water/alite ratio were small and did not provide any obvious correlation with drying shrinkage. The analyses were in good agreement with published data for hydrated portland cement, and indicated the presence of derivatized silicates with molecular weights of about 1130 and 1740 in addition to monomeric, dimeric and highly condensed silica. The derivatization reaction was not noticeably affected by the presence of water in the pores of the hydrated alite.

ZusammenfassungWir untersuchten die Auswirkungen ausgedehnter Trocknungszeiten und verschiedener Wasser/Alit-Mischungsverhältnisse auf die Silikatstruktur hydratisierter Alit-Pasten, unter Anwendung der Gel-Permeations- Chromatographie von Trimethylsilyl-Derivaten. Die Auswirkungen sowohl des Trochnens wie des Wasser/Alit-Verhältnisses waren gering, und es liess sich kein Zusammenhang zum Trocknungsschwinden erkennen. Die Analysen standen in Ueberinstimmung mit veröffentlichten Daten für hydratisierten Portland Zement und wiesen auf Silyderivate mit Molekulargewichten von rund 1130 und 1740 neben Monomeren, Dimeren und hochpolymerisierten Silikaten hin. Wir fanden keine Anzeichen dafür, dass die Silylierungsreaktion durch Porenwasser im hydratisierten Alit beeinflusst würde.