Properties of self-compacting concrete prepared with recycled glass aggregate
AbstractThe effects of recycled glass (RG) cullet on fresh and hardened properties of self-compacting concrete (SCC) were investigated. RG was used to replace river sand (in proportions of 10%, 20% and 30%), and 10mm granite (5%, 10% and 15%) in making the SCC concrete mixes. Fly ash was used in the concrete mixes to suppress the potential alkali-silica reaction. The experimental results showed that the slump flow, blocking ratio, air content of the RG–SCC mixes increased with increasing recycled glass content. The compressive strength, tensile splitting strength and static modulus of elasticity of the RG–SCC mixes were decreased with an increase in recycled glass aggregate content. Moreover, the resistance to chloride ion penetration increased and the drying shrinkage of the RG–SCC mixes decreased when the recycled glass content increased. The results showed that it is feasible to produce SCC with recycled glass cullet.
Properties of self-compacting concrete prepared with recycled glass aggregate
AbstractThe effects of recycled glass (RG) cullet on fresh and hardened properties of self-compacting concrete (SCC) were investigated. RG was used to replace river sand (in proportions of 10%, 20% and 30%), and 10mm granite (5%, 10% and 15%) in making the SCC concrete mixes. Fly ash was used in the concrete mixes to suppress the potential alkali-silica reaction. The experimental results showed that the slump flow, blocking ratio, air content of the RG–SCC mixes increased with increasing recycled glass content. The compressive strength, tensile splitting strength and static modulus of elasticity of the RG–SCC mixes were decreased with an increase in recycled glass aggregate content. Moreover, the resistance to chloride ion penetration increased and the drying shrinkage of the RG–SCC mixes decreased when the recycled glass content increased. The results showed that it is feasible to produce SCC with recycled glass cullet.
Properties of self-compacting concrete prepared with recycled glass aggregate
Kou, S.C. (author) / Poon, C.S. (author)
Cement and Concrete Composites ; 31 ; 107-113
2008-12-05
7 pages
Article (Journal)
Electronic Resource
English
Properties of self-compacting concrete prepared with recycled glass aggregate
| Online Contents | 2009
Properties of self-compacting concrete prepared with recycled glass aggregate
| Online Contents | 2009
Properties of self-compacting concrete prepared with coarse recycled concrete aggregate
| British Library Online Contents | 2010
Self-compacting concrete incorporating recycled aggregate
| British Library Conference Proceedings | 2002