Fatigue damage accumulation in carbon/epoxy laminated composites
AbstractThe precise prediction of fatigue damage progress and fatigue life in laminated composites has been always a concern to designers. The present work is focused on the fatigue damage mechanisms and damage accumulation rate in laminated composites. Results showed that the dominant damage mechanism depends on the applied stress and total delamination only observed under the cyclic stress of less than 0.7σUTS. Under high cyclic stress, transverse cracks in 45° ply appear and its density rapidly increases to the characteristic damage state (CDS). The obtained results showed that high-stress peaks (HSP) have remarkable effect on the fatigue life and predictions based on Palmgren–Miner’s rule showed considerable deviations from experimental results, whereas the new cumulative damage model presented in this work provided acceptable consistency with experimental results in the entire range of applied stress.
Fatigue damage accumulation in carbon/epoxy laminated composites
AbstractThe precise prediction of fatigue damage progress and fatigue life in laminated composites has been always a concern to designers. The present work is focused on the fatigue damage mechanisms and damage accumulation rate in laminated composites. Results showed that the dominant damage mechanism depends on the applied stress and total delamination only observed under the cyclic stress of less than 0.7σUTS. Under high cyclic stress, transverse cracks in 45° ply appear and its density rapidly increases to the characteristic damage state (CDS). The obtained results showed that high-stress peaks (HSP) have remarkable effect on the fatigue life and predictions based on Palmgren–Miner’s rule showed considerable deviations from experimental results, whereas the new cumulative damage model presented in this work provided acceptable consistency with experimental results in the entire range of applied stress.
Fatigue damage accumulation in carbon/epoxy laminated composites
Aghazadeh Mohandesi, J. (author) / Majidi, B. (author)
2008-09-05
7 pages
Article (Journal)
Electronic Resource
English
Fatigue damage accumulation in carbon/epoxy laminated composites
| British Library Online Contents | 2009
Damage modelling of laminated carbon/epoxy composites under static and fatigue loadings
| British Library Online Contents | 2002
Fatigue Damage in Laminated Composites
| British Library Online Contents | 1993
Overlay patch repair of scratch damage in carbon fiber/epoxy laminated composites
| British Library Online Contents | 2013
Fatigue damage behaviors of carbon fiber-reinforced epoxy composites containing nanoclay
| British Library Online Contents | 2010