Electroless deposition of Ni–P–B4C composite coating on AZ91D magnesium alloy and investigation on its wear and corrosion resistance
AbstractIn the present work, the effect of applying ternary Ni–P–B4C composite coating from an electroless plating bath containing sulfate nickel, sodium hypophosphate and suspended B4C particles, on the corrosion and wear resistance of an AZ91D, high aluminum cast magnesium alloy, was investigated. Regarding low corrosion resistance of magnesium alloys, chromium oxide plus HF (Hydro Fluoric Acid) pretreatment was applied to prepare the substrate for coating treatment in electroless bath. The pH value and temperature of the electroless bath were 9 and 82°C, respectively. The coating was characterized for its micro structure, morphology, microhardness, wear and corrosion resistance. SEM (Scanning Electron Microscope) observation showed dense and coarse nodules in the ternary composite coating and the cross section of Ni–P–B4C coating offered presence of well dispersed B4C particles in the coating. The hardness of the Ni–P–B4C composite coatings was around 1200MPa, more than what can be obtained for Ni–P coatings (about 700MPa). The wear test which was carried out by using pin on disc method, showed that ternary Ni–P–B4C composite coating had a good wear resistance and more superior than Ni-P coating. The polarization test results for ternary Ni–P–B4C composite coating exhibited good corrosion resistance properties in protecting the AZ91D magnesium alloy, but not better than Ni–P coating.
Electroless deposition of Ni–P–B4C composite coating on AZ91D magnesium alloy and investigation on its wear and corrosion resistance
AbstractIn the present work, the effect of applying ternary Ni–P–B4C composite coating from an electroless plating bath containing sulfate nickel, sodium hypophosphate and suspended B4C particles, on the corrosion and wear resistance of an AZ91D, high aluminum cast magnesium alloy, was investigated. Regarding low corrosion resistance of magnesium alloys, chromium oxide plus HF (Hydro Fluoric Acid) pretreatment was applied to prepare the substrate for coating treatment in electroless bath. The pH value and temperature of the electroless bath were 9 and 82°C, respectively. The coating was characterized for its micro structure, morphology, microhardness, wear and corrosion resistance. SEM (Scanning Electron Microscope) observation showed dense and coarse nodules in the ternary composite coating and the cross section of Ni–P–B4C coating offered presence of well dispersed B4C particles in the coating. The hardness of the Ni–P–B4C composite coatings was around 1200MPa, more than what can be obtained for Ni–P coatings (about 700MPa). The wear test which was carried out by using pin on disc method, showed that ternary Ni–P–B4C composite coating had a good wear resistance and more superior than Ni-P coating. The polarization test results for ternary Ni–P–B4C composite coating exhibited good corrosion resistance properties in protecting the AZ91D magnesium alloy, but not better than Ni–P coating.
Electroless deposition of Ni–P–B4C composite coating on AZ91D magnesium alloy and investigation on its wear and corrosion resistance
Araghi, A. (author) / Paydar, M.H. (author)
2009-12-27
5 pages
Article (Journal)
Electronic Resource
English
| British Library Online Contents | 2010
Electroless deposition of Ni-W-P coating on AZ91D magnesium alloy
| British Library Online Contents | 2007
| British Library Online Contents | 2018
Corrosion of AZ91D magnesium alloy with a chemical conversion coating and electroless nickel layer
| British Library Online Contents | 2004
| British Library Online Contents | 2014