A comparative study of the amaranth azo dye adsorption/desorption from aqueous solutions by layered double hydroxides
AbstractMagnesium aluminum layered double hydroxides (LDH) were synthesized by the co-precipitation method with nitrate and carbonate as interlayer anion (MgAlNO3 and MgAlCO3) followed by the calcination of a carbonate containing LDH sample to obtain the mixed oxide MgAl500. The resulting materials were characterized by several physicochemical techniques. Calcined and uncalcined LDHs were used as adsorbents to remove the amaranth azo dye in an aqueous solution. Adsorption results indicated that MgAl500 had a greater adsorption capacity (1.6mmol·g−1) than non-calcined LDHs (0.8 and 0.2mmol·g−1for MgAlNO3 and MgAlCO3, respectively). Isotherms showed that the adsorption of the dye was consistent with the Langmuir model. The kinetic experiments of dye adsorption showed that the system reached the adsorption equilibrium in 3h for the three adsorbents. The kinetic data fitted well with the pseudo-second order model. Powder X ray diffraction patterns of the adsorption products suggest that adsorbed amaranth anion was intercalated in the MgAlNO3 interlayers by anion exchange and in the MgAl500 by the rehydration and reconstruction process, according to the value of the basal space d003=17.7Å. Whereas in the case of MgAlCO3, .it was probably adsorbed on the external particle surface. The influence of common inorganic anions present in the solution was also studied and a decrease in the dye removal was observed in the following order HPO42−>CO32–>SO42−>Cl-. The dye desorption was tested with carbonate and phosphate solution and it was partial in all cases. The recyclability of the used adsorbents was performed by calcinations, and the percentage of removal decreases after the first cycle for MgAlNO3 and MgAl500. Dye removal improved after the first cycle then decreased after the second cycle for MgAlCO3.
HighlightsAmaranth dye was successfully adsorbed by intercalation on MgAlNO3 and calcined MgAlCO3 (MgAl500).Adsorption of the dye occurs via anion exchange for MgAlNO3 and via reconstruction for MgAl500.Lower amounts were adsorbed on uncalcinated MgAlCO3, but this adsorbent has the best recyclability potential.The adsorption was affected by the presence of the inorganic anions in the order HPO42−>CO32–>SO42−>Cl−.
A comparative study of the amaranth azo dye adsorption/desorption from aqueous solutions by layered double hydroxides
AbstractMagnesium aluminum layered double hydroxides (LDH) were synthesized by the co-precipitation method with nitrate and carbonate as interlayer anion (MgAlNO3 and MgAlCO3) followed by the calcination of a carbonate containing LDH sample to obtain the mixed oxide MgAl500. The resulting materials were characterized by several physicochemical techniques. Calcined and uncalcined LDHs were used as adsorbents to remove the amaranth azo dye in an aqueous solution. Adsorption results indicated that MgAl500 had a greater adsorption capacity (1.6mmol·g−1) than non-calcined LDHs (0.8 and 0.2mmol·g−1for MgAlNO3 and MgAlCO3, respectively). Isotherms showed that the adsorption of the dye was consistent with the Langmuir model. The kinetic experiments of dye adsorption showed that the system reached the adsorption equilibrium in 3h for the three adsorbents. The kinetic data fitted well with the pseudo-second order model. Powder X ray diffraction patterns of the adsorption products suggest that adsorbed amaranth anion was intercalated in the MgAlNO3 interlayers by anion exchange and in the MgAl500 by the rehydration and reconstruction process, according to the value of the basal space d003=17.7Å. Whereas in the case of MgAlCO3, .it was probably adsorbed on the external particle surface. The influence of common inorganic anions present in the solution was also studied and a decrease in the dye removal was observed in the following order HPO42−>CO32–>SO42−>Cl-. The dye desorption was tested with carbonate and phosphate solution and it was partial in all cases. The recyclability of the used adsorbents was performed by calcinations, and the percentage of removal decreases after the first cycle for MgAlNO3 and MgAl500. Dye removal improved after the first cycle then decreased after the second cycle for MgAlCO3.
HighlightsAmaranth dye was successfully adsorbed by intercalation on MgAlNO3 and calcined MgAlCO3 (MgAl500).Adsorption of the dye occurs via anion exchange for MgAlNO3 and via reconstruction for MgAl500.Lower amounts were adsorbed on uncalcinated MgAlCO3, but this adsorbent has the best recyclability potential.The adsorption was affected by the presence of the inorganic anions in the order HPO42−>CO32–>SO42−>Cl−.
A comparative study of the amaranth azo dye adsorption/desorption from aqueous solutions by layered double hydroxides
Abdellaoui, K. (author) / Pavlovic, I. (author) / Bouhent, M. (author) / Benhamou, A. (author) / Barriga, C. (author)
Applied Clay Science ; 143 ; 142-150
2017-03-14
9 pages
Article (Journal)
Electronic Resource
English
Adsorption of phosphate by layered double hydroxides in aqueous solutions
| Online Contents | 2006
Adsorption of Cr(VI) in layered double hydroxides
| Online Contents | 1998
Electrode Properties of Nickel-Aluminum Layered Double Hydroxides in Aqueous Electrolyte Solutions
| British Library Online Contents | 2013