Corrosion inhibition effect of zeolitic imidazolate framework in chloride-contaminated cement pore solution under elevated temperatures
Graphical abstract Display Omitted
Highlights Higher activation energy (Ea) was relevant to steel corrosion in SPS with ZIF-8. The elevated temperature led to unstable adsorption and agglomeration of ZIF-8. The inhibition efficiency of ZIF-8 was obviously reduced at elevated temperature.
Abstract The elevated temperature significantly influences the adsorption behavior of corrosion inhibitors, and subsequently reduces its inhibition efficiency for the reinforcement. In this study, the inhibition effect of novel zeolitic imidazolate framework (ZIF-8) corrosion inhibitor on the reinforcement under the elevated temperature (from 25 °C to 55 °C) was extensively investigated in simulated cement pore solution (SPS) by electrochemical measurement together with SEM observation and Raman analysis. The thermodynamic and kinetic parameters for corrosion reaction of the reinforcement were also calculated. At 25 °C, ZIF-8 corrosion inhibitor efficiently reduced corrosion rate of the reinforcement in SPS, exhibiting very high inhibition efficiency. Higher activation energy (Ea) for corrosion reaction was relevant to ZIF-8 containing specimen, indicating that the corrosion rate of the steel was significantly accelerated in SPS with ZIF-8 under the elevated temperature. ZIF-8 corrosion inhibitor still halted corrosion of the steel under elevated temperatures; however, unstable adsorption and agglomeration of ZIF-8 was relevant at the elevated temperature. As a result, its inhibition efficiency was significantly reduced from 87.8% at 25 °C to only 18.7% at 55 °C.
Corrosion inhibition effect of zeolitic imidazolate framework in chloride-contaminated cement pore solution under elevated temperatures
Graphical abstract Display Omitted
Highlights Higher activation energy (Ea) was relevant to steel corrosion in SPS with ZIF-8. The elevated temperature led to unstable adsorption and agglomeration of ZIF-8. The inhibition efficiency of ZIF-8 was obviously reduced at elevated temperature.
Abstract The elevated temperature significantly influences the adsorption behavior of corrosion inhibitors, and subsequently reduces its inhibition efficiency for the reinforcement. In this study, the inhibition effect of novel zeolitic imidazolate framework (ZIF-8) corrosion inhibitor on the reinforcement under the elevated temperature (from 25 °C to 55 °C) was extensively investigated in simulated cement pore solution (SPS) by electrochemical measurement together with SEM observation and Raman analysis. The thermodynamic and kinetic parameters for corrosion reaction of the reinforcement were also calculated. At 25 °C, ZIF-8 corrosion inhibitor efficiently reduced corrosion rate of the reinforcement in SPS, exhibiting very high inhibition efficiency. Higher activation energy (Ea) for corrosion reaction was relevant to ZIF-8 containing specimen, indicating that the corrosion rate of the steel was significantly accelerated in SPS with ZIF-8 under the elevated temperature. ZIF-8 corrosion inhibitor still halted corrosion of the steel under elevated temperatures; however, unstable adsorption and agglomeration of ZIF-8 was relevant at the elevated temperature. As a result, its inhibition efficiency was significantly reduced from 87.8% at 25 °C to only 18.7% at 55 °C.
Corrosion inhibition effect of zeolitic imidazolate framework in chloride-contaminated cement pore solution under elevated temperatures
Wang, Yangyang (author) / Chen, Ting (author) / Wang, Hao (author) / Hu, Jie (author) / Ma, Yuwei (author) / Wei, Jiangxiong (author) / Yin, Suhong (author) / Yu, Qijun (author)
2022-05-31
Article (Journal)
Electronic Resource
English
Synthesis of zeolitic imidazolate framework nanocrystals
| British Library Online Contents | 2014
Synthesis of zeolitic imidazolate framework nanocrystals
| British Library Online Contents | 2014
Synthesis and Application of Zeolitic Imidazolate Framework (ZIF-8) in Cement Composites
| Springer Verlag | 2024
Adsorptive removal of phenol from aqueous solution with zeolitic imidazolate framework-67
| Online Contents | 2016