Mechanical behaviour of fresh concrete
AbstractThe shear strength characteristics of fresh concrete were studied through the use of a triaxial compression apparatus on concrete cylinders 100 mm in diameter and 200 mm high at 21°C and 4°C for set times ranging from 40 minutes to 160 minutes. The test results were analyzed by the shear strength theories of Mohr-Coulomb and Rowe for each time-temperature combination. The angle of internal friction was found to be a constant property of the mix in the range of 37° to 41° for a 10% failure strain when analyzed by Mohr-Coulomb. Rowe's analysis gave friction angles of 18° to 21° for a 10% failure strain. Both theories indicate that the cohesion of fresh concrete is initially zero and increases with set time.
RésuméLa résistance au cisaillement du béton frais a été étudiée avec l'aide d'un appareil triaxial sur des échantillons de 100 mm de diamétre par 200 mm en grandeur à 21°C et 4°C pour une durée de 40 minutes à 160 minutes. Par la suite les résultats ont été analysés employant les théories de Mohr-Coulomb et Rowe et ont été exprimés comme les deux paramètres de cohésion et de frottement pour chaque combinaison de température et de durée. On a déduit que l'angle de frottement était une propriété constante du mélange et résidait entre 37° et 41° pour une déformation finale de 10% utilisant la théorie de Mohr-Coulomb. L'analyse de Rowe a donné des angles de frottement de 18° à 21° pour une déformation finale de 10%. Les deux théories ont indiqué que la cohésion était initialement zéro et qu'elle s'était agrandit avec le temps.
Mechanical behaviour of fresh concrete
AbstractThe shear strength characteristics of fresh concrete were studied through the use of a triaxial compression apparatus on concrete cylinders 100 mm in diameter and 200 mm high at 21°C and 4°C for set times ranging from 40 minutes to 160 minutes. The test results were analyzed by the shear strength theories of Mohr-Coulomb and Rowe for each time-temperature combination. The angle of internal friction was found to be a constant property of the mix in the range of 37° to 41° for a 10% failure strain when analyzed by Mohr-Coulomb. Rowe's analysis gave friction angles of 18° to 21° for a 10% failure strain. Both theories indicate that the cohesion of fresh concrete is initially zero and increases with set time.
RésuméLa résistance au cisaillement du béton frais a été étudiée avec l'aide d'un appareil triaxial sur des échantillons de 100 mm de diamétre par 200 mm en grandeur à 21°C et 4°C pour une durée de 40 minutes à 160 minutes. Par la suite les résultats ont été analysés employant les théories de Mohr-Coulomb et Rowe et ont été exprimés comme les deux paramètres de cohésion et de frottement pour chaque combinaison de température et de durée. On a déduit que l'angle de frottement était une propriété constante du mélange et résidait entre 37° et 41° pour une déformation finale de 10% utilisant la théorie de Mohr-Coulomb. L'analyse de Rowe a donné des angles de frottement de 18° à 21° pour une déformation finale de 10%. Les deux théories ont indiqué que la cohésion était initialement zéro et qu'elle s'était agrandit avec le temps.
Mechanical behaviour of fresh concrete
Alexandridis, A. (author) / Gardner, N.J. (author)
Cement and Concrete Research ; 11 ; 323-339
1980-12-19
17 pages
Article (Journal)
Electronic Resource
English
Modelling the Rheological Behaviour of Fresh Concrete
| British Library Conference Proceedings | 1993
P25.- THE LEACHING BEHAVIOUR OF FRESH CONCRETE
| British Library Conference Proceedings | 2003
Mechanical properties of fresh concrete for concrete products
Engineering Index Backfile | 1963
Computer Modelling of the Behaviour of Fresh Concrete
| British Library Conference Proceedings | 1996