Thermal stability of ettringite in alkaline solutions at 80 °C
AbstractThe thermal stability of synthetic ettringite was examined in NaOH solutions up to 1 M after 12 h of heat treatment at 80 °C, with or without the coexistence of C3S in the system. Ettringite was found to convert to the U phase, a sodium-substituted AFm phase, over the heat treatment in the absence of C3S. The presence of C3S, leading to C-S-H formation, prevents the U phase formation and results in the conversion of ettringite to monosulfate. Sulfate ions generated from ettringite decomposition mostly remain in the solution, but some is incorporated into C-S-H. During subsequent storage at room temperature, the majority of monosulfate slowly converts back to secondary ettringite under moist conditions, using the supply of sulfate ions from the solution and C-S-H. The observations support the current mechanism of delayed ettringite formation (DEF).
Thermal stability of ettringite in alkaline solutions at 80 °C
AbstractThe thermal stability of synthetic ettringite was examined in NaOH solutions up to 1 M after 12 h of heat treatment at 80 °C, with or without the coexistence of C3S in the system. Ettringite was found to convert to the U phase, a sodium-substituted AFm phase, over the heat treatment in the absence of C3S. The presence of C3S, leading to C-S-H formation, prevents the U phase formation and results in the conversion of ettringite to monosulfate. Sulfate ions generated from ettringite decomposition mostly remain in the solution, but some is incorporated into C-S-H. During subsequent storage at room temperature, the majority of monosulfate slowly converts back to secondary ettringite under moist conditions, using the supply of sulfate ions from the solution and C-S-H. The observations support the current mechanism of delayed ettringite formation (DEF).
Thermal stability of ettringite in alkaline solutions at 80 °C
Shimada, Yukie (author) / Young, J.Francis (author)
Cement and Concrete Research ; 34 ; 2261-2268
2004-04-07
8 pages
Article (Journal)
Electronic Resource
English
Thermal stability of ettringite in alkaline solutions at 80 degreeC
| British Library Online Contents | 2004
Thermal stability of ettringite in alkaline solutions at 80 (degree)C
| Online Contents | 2004
Thermal stability of ettringite in alkaline solutions at 80 degree C
| Tema Archive | 2004
The Thermodynamic Stability of Ettringite
| British Library Online Contents | 1999
Thermal stability and decomposition mechanisms of ettringite at <120degreeC
| British Library Online Contents | 2001