Characteristics of calcined natural zeolites for use in high-performance pozzolan blended cements
Highlights Effects of calcination on properties of natural zeolites were investigated. Physical, mineralogical and pozzolanic properties were determined. Calcined forms showed less water demand and higher strength activity in blended cements. Strength performance was attributed to the porosity and pore size distribution.
Abstract Two natural zeolites with different characteristics were calcined at various temperatures in order to improve the benefits provided by their use in blended cements as cement replacement material. Natural zeolites were firstly characterized for their crystallinity by X-ray diffraction analysis, specific surface area by nitrogen absorption, and pozzolanic activity by electrical conductivity method, before and after the calcination. In order to assess the performance of calcined natural zeolite as cement replacement material, blended Portland cement pastes and mortars with raw and calcined zeolites were tested for their water requirement, free lime content, pore size distribution and compressive strength. The experimental results indicated that calcined zeolites are more desirable with lower water requirement and higher strength performance as cement replacement material than the raw zeolites. Blended cement with calcined natural zeolite showed higher compressive strength performance, when compared to that with the raw zeolite due to decreased porosity and refined pore structure of the hardened cementitious system.
Characteristics of calcined natural zeolites for use in high-performance pozzolan blended cements
Highlights Effects of calcination on properties of natural zeolites were investigated. Physical, mineralogical and pozzolanic properties were determined. Calcined forms showed less water demand and higher strength activity in blended cements. Strength performance was attributed to the porosity and pore size distribution.
Abstract Two natural zeolites with different characteristics were calcined at various temperatures in order to improve the benefits provided by their use in blended cements as cement replacement material. Natural zeolites were firstly characterized for their crystallinity by X-ray diffraction analysis, specific surface area by nitrogen absorption, and pozzolanic activity by electrical conductivity method, before and after the calcination. In order to assess the performance of calcined natural zeolite as cement replacement material, blended Portland cement pastes and mortars with raw and calcined zeolites were tested for their water requirement, free lime content, pore size distribution and compressive strength. The experimental results indicated that calcined zeolites are more desirable with lower water requirement and higher strength performance as cement replacement material than the raw zeolites. Blended cement with calcined natural zeolite showed higher compressive strength performance, when compared to that with the raw zeolite due to decreased porosity and refined pore structure of the hardened cementitious system.
Characteristics of calcined natural zeolites for use in high-performance pozzolan blended cements
Küçükyıldırım, E. (author) / Uzal, B. (author)
Construction and Building Materials ; 73 ; 229-234
2014-09-24
6 pages
Article (Journal)
Electronic Resource
English
Characteristics of calcined natural zeolites for use in high-performance pozzolan blended cements
| Online Contents | 2014
Behavior of Concrete Containing Alternative Pozzolan Calcined Marl Blended Cement
| BASE | 2020
Hydration study of ternary blended cements containing ferronickel slag and natural pozzolan
| Online Contents | 2015
Effect of large amounts of natural pozzolan addition on properties of blended cements
| Tema Archive | 2005