Effect of tool rotational speed and pin profile on microstructure and tensile strength of dissimilar friction stir welded AA5083-H111 and AA6351-T6 aluminum alloys
Graphical abstract Display Omitted Highlights ► Dissimilar friction stir welding of AA5083-H111 and AA6351-T6. ► Tool rotational speed and pin profile affect weld microstructure. ► Weld zone exhibits three kinds of microstructures. ► Material flow behavior during welding influences tensile strength.
Abstract The relatively new welding process friction stir welding (FSW) was applied in this research work to join 6mm thick dissimilar aluminum alloys AA5083-H111 and AA6351-T6. The effect of tool rotational speed and pin profile on the microstructure and tensile strength of the joints were studied. Dissimilar joints were made using three different tool rotational speeds of 600rpm, 950rpm and 1300rpm and five different tool pin profiles of straight square (SS), straight hexagon (SH), straight octagon (SO), tapered square (TS), and tapered octagon (TO). Three different regions namely unmixed region, mechanically mixed region and mixed flow region were observed in the weld zone. The tool rotational speed and pin profile considerably influenced the microstructure and tensile strength of the joints. The joint which was fabricated using tool rotational speed of 950rpm and straight square pin profile yielded highest tensile strength of 273MPa. The two process parameters affected the joint strength due to variations in material flow behavior, loss of cold work in the HAZ of AA5083 side, dissolution and over aging of precipitates of AA6351 side and formation of macroscopic defects in the weld zone.
Effect of tool rotational speed and pin profile on microstructure and tensile strength of dissimilar friction stir welded AA5083-H111 and AA6351-T6 aluminum alloys
Graphical abstract Display Omitted Highlights ► Dissimilar friction stir welding of AA5083-H111 and AA6351-T6. ► Tool rotational speed and pin profile affect weld microstructure. ► Weld zone exhibits three kinds of microstructures. ► Material flow behavior during welding influences tensile strength.
Abstract The relatively new welding process friction stir welding (FSW) was applied in this research work to join 6mm thick dissimilar aluminum alloys AA5083-H111 and AA6351-T6. The effect of tool rotational speed and pin profile on the microstructure and tensile strength of the joints were studied. Dissimilar joints were made using three different tool rotational speeds of 600rpm, 950rpm and 1300rpm and five different tool pin profiles of straight square (SS), straight hexagon (SH), straight octagon (SO), tapered square (TS), and tapered octagon (TO). Three different regions namely unmixed region, mechanically mixed region and mixed flow region were observed in the weld zone. The tool rotational speed and pin profile considerably influenced the microstructure and tensile strength of the joints. The joint which was fabricated using tool rotational speed of 950rpm and straight square pin profile yielded highest tensile strength of 273MPa. The two process parameters affected the joint strength due to variations in material flow behavior, loss of cold work in the HAZ of AA5083 side, dissolution and over aging of precipitates of AA6351 side and formation of macroscopic defects in the weld zone.
Effect of tool rotational speed and pin profile on microstructure and tensile strength of dissimilar friction stir welded AA5083-H111 and AA6351-T6 aluminum alloys
Palanivel, R. (author) / Koshy Mathews, P. (author) / Murugan, N. (author) / Dinaharan, I. (author)
2012-03-16
10 pages
Article (Journal)