Full-Range fatigue behavior of NSM CFRP-to-Concrete bonded joints
Highlights Degradation of local bond strength of FRP-to-concrete bonded joints subject to direct pull-out fatigue loading is investigated. Effect of various parameters on fatigue bond behavior and life is considered. Higher fatigue load ranges accelerated local bond degradation drastically leading to a much shorter fatigue life of bonded joints.
Abstract The interfacial bond characteristics and failure mechanism of near-surface mounted (NSM) fiber reinforced polymer (FRP) composites in concrete under fatigue loading are less understood compared to their bond behavior under static loading. In this paper, degradation of the local bond strength of FRP-to-concrete bonded joints subjected to direct pull-out fatigue loading is presented for both carbon FRP (CFRP) rods and strips under different fatigue load ranges, i.e., 10–50%, 10–60%, and 10–70%, of the corresponding static load-carrying capacity. The interfacial debonding between FRP and adhesive was observed during fatigue cycles for CFRP rod specimens to different extents. Specimens using CFRP rods with sand-coated and spirally wound surface treatment presented a higher local bond strength and a slower degradation rate, as compared to the ones using CFRP rods with roughened or sand-coated treatment. Using epoxy adhesives with higher strengths benefitted the fatigue bond performance of the tested specimens in terms of local bond strength and stable behavior. Higher fatigue load ranges substantially accelerated the local bond degradation resulting in a much shorter fatigue life of the bonded joints.
Full-Range fatigue behavior of NSM CFRP-to-Concrete bonded joints
Highlights Degradation of local bond strength of FRP-to-concrete bonded joints subject to direct pull-out fatigue loading is investigated. Effect of various parameters on fatigue bond behavior and life is considered. Higher fatigue load ranges accelerated local bond degradation drastically leading to a much shorter fatigue life of bonded joints.
Abstract The interfacial bond characteristics and failure mechanism of near-surface mounted (NSM) fiber reinforced polymer (FRP) composites in concrete under fatigue loading are less understood compared to their bond behavior under static loading. In this paper, degradation of the local bond strength of FRP-to-concrete bonded joints subjected to direct pull-out fatigue loading is presented for both carbon FRP (CFRP) rods and strips under different fatigue load ranges, i.e., 10–50%, 10–60%, and 10–70%, of the corresponding static load-carrying capacity. The interfacial debonding between FRP and adhesive was observed during fatigue cycles for CFRP rod specimens to different extents. Specimens using CFRP rods with sand-coated and spirally wound surface treatment presented a higher local bond strength and a slower degradation rate, as compared to the ones using CFRP rods with roughened or sand-coated treatment. Using epoxy adhesives with higher strengths benefitted the fatigue bond performance of the tested specimens in terms of local bond strength and stable behavior. Higher fatigue load ranges substantially accelerated the local bond degradation resulting in a much shorter fatigue life of the bonded joints.
Full-Range fatigue behavior of NSM CFRP-to-Concrete bonded joints
Wang, Xun (author) / Cheng, Lijuan (author)
Engineering Structures ; 295
2023-08-24
Article (Journal)
Electronic Resource
English
Full-range behavior of FRP-to-concrete bonded joints
Online Contents | 2004
|Full-range behavior of FRP-to-concrete bonded joints
Elsevier | 2003
|Behavior of Adhesively Bonded Concrete-CFRP Joints at Low and High Temperatures
British Library Online Contents | 2001
|Damage in adhesively bonded CFRP joints: Sinusoidal and impact-fatigue
British Library Online Contents | 2008
|