Effect of phlogopite mica on alkali-aggregate expansion in concrete
AbstractThe tensile strength of concrete is increased by the addition of high aspect-ratio mica reinforcement. Phlogopite mica contains about 10% K2O; soluble K+ would contribute to the alkalinity of the pore solution in concrete enhancing its potential expansivity if it is made with alkali-expansive aggregate. Electron microprobe analysis confirms that the solubility of K+ from phlogopite in cement paste, about 0.09% is the same as in mixed calcium-sodium-hydroxide solutions. The addition of 1.5% by volume of phlogopite to concrete prisms made with alkali-carbonate expansive aggregates caused a small increase in the rate of expansion of prisms made with both high and low alkali cement. It is concluded that the addition of small quantities of phlogopite as a reinforcement in concrete is not a cause for concern, although caution should be exercised in adding larger volumes to concrete made with potentially alkali-expensive aggregate.
RésuméL'addition d'une armature de mica possédant un rapport de l'envergure à la profondeur élevé augmente la résistance à la traction du béton. Le mica phlogopite contient à peu près 10% de K2O; le soluble (K+) contribue à l'alcalinité de la solution poreuse du béton, accentuant l'expansibilité potentielle du béton composé d'un agrégat alcali-expansif. L'addition d'une quantité de phlogopite équivalant à 1.5% du volume à des prismes de béton faits d'un agrégat d'alcali-carbonate expansif a provoqué un léger accroissement de la vitesse d'expansion des prismes, que ceux-ci aient été composés d'un ciment fortement ou faiblement alcalinisé. On peut conclure que l'addition d'une petite quantité de phlogopite pour renforcer le béton ne devrait pas être un sujet de préoccupation, bien qu'on devrait exercer une certaine prudence lorsqu'on en ajoute de plus grandes quantités à un volume de béton composé d'un agrégat alcali-expansif.
Effect of phlogopite mica on alkali-aggregate expansion in concrete
AbstractThe tensile strength of concrete is increased by the addition of high aspect-ratio mica reinforcement. Phlogopite mica contains about 10% K2O; soluble K+ would contribute to the alkalinity of the pore solution in concrete enhancing its potential expansivity if it is made with alkali-expansive aggregate. Electron microprobe analysis confirms that the solubility of K+ from phlogopite in cement paste, about 0.09% is the same as in mixed calcium-sodium-hydroxide solutions. The addition of 1.5% by volume of phlogopite to concrete prisms made with alkali-carbonate expansive aggregates caused a small increase in the rate of expansion of prisms made with both high and low alkali cement. It is concluded that the addition of small quantities of phlogopite as a reinforcement in concrete is not a cause for concern, although caution should be exercised in adding larger volumes to concrete made with potentially alkali-expensive aggregate.
RésuméL'addition d'une armature de mica possédant un rapport de l'envergure à la profondeur élevé augmente la résistance à la traction du béton. Le mica phlogopite contient à peu près 10% de K2O; le soluble (K+) contribue à l'alcalinité de la solution poreuse du béton, accentuant l'expansibilité potentielle du béton composé d'un agrégat alcali-expansif. L'addition d'une quantité de phlogopite équivalant à 1.5% du volume à des prismes de béton faits d'un agrégat d'alcali-carbonate expansif a provoqué un léger accroissement de la vitesse d'expansion des prismes, que ceux-ci aient été composés d'un ciment fortement ou faiblement alcalinisé. On peut conclure que l'addition d'une petite quantité de phlogopite pour renforcer le béton ne devrait pas être un sujet de préoccupation, bien qu'on devrait exercer une certaine prudence lorsqu'on en ajoute de plus grandes quantités à un volume de béton composé d'un agrégat alcali-expansif.
Effect of phlogopite mica on alkali-aggregate expansion in concrete
Grattan-Bellew, P.E. (author) / Beaudoin, J.J. (author)
Cement and Concrete Research ; 10 ; 789-797
1980-08-05
9 pages
Article (Journal)
Electronic Resource
English
Depleted brittle mica structure determination in Ba-phlogopite glass–ceramics
| British Library Online Contents | 2012
The Effect of Phlogopite Mica on the Sintering Point and Colour of a Claybody
| British Library Online Contents | 1997
Effect of Slag on Expansion Due to Alkali-Aggregate Reaction in Concrete
| Online Contents | 1998