An investigation on the microstructure and mechanical properties of direct-quenched and tempered AISI 4140 steel
AbstractDirect quenching (DQ) process is an appropriate method in steels heat treatment field. This method enhances production rate, reduces energy consumption and decreases environment contamination. In this study hot-rolled AISI 4140 steel billets with different diameters (75,80,85,100,105 and 115mm) and 20m length were quenched directly in a water tank. Also some samples with similar size and composition were provided by conventional reheating, quenching and tempering (RQ) heat treatment process. The quenched samples were tempered at the temperature of 630°C for 2h. Mechanical properties of heat treated samples including tensile strength, yield strength, elongation, hardness and impact toughness were measured. Also, the microstructure and harden-ability of this steel were investigated under various conditions and the results were compared to RQ heat treated products. The results showed that direct quenching and tempering processes (DQ–T) is due to enhance of mechanical properties such as tensile strength and harden-ability of AISI 4140 and it is affected by various parameters such as steel temperature before quenching, water temperature, quenching time and also billet size.
An investigation on the microstructure and mechanical properties of direct-quenched and tempered AISI 4140 steel
AbstractDirect quenching (DQ) process is an appropriate method in steels heat treatment field. This method enhances production rate, reduces energy consumption and decreases environment contamination. In this study hot-rolled AISI 4140 steel billets with different diameters (75,80,85,100,105 and 115mm) and 20m length were quenched directly in a water tank. Also some samples with similar size and composition were provided by conventional reheating, quenching and tempering (RQ) heat treatment process. The quenched samples were tempered at the temperature of 630°C for 2h. Mechanical properties of heat treated samples including tensile strength, yield strength, elongation, hardness and impact toughness were measured. Also, the microstructure and harden-ability of this steel were investigated under various conditions and the results were compared to RQ heat treated products. The results showed that direct quenching and tempering processes (DQ–T) is due to enhance of mechanical properties such as tensile strength and harden-ability of AISI 4140 and it is affected by various parameters such as steel temperature before quenching, water temperature, quenching time and also billet size.
An investigation on the microstructure and mechanical properties of direct-quenched and tempered AISI 4140 steel
Meysami, A.H. (author) / Ghasemzadeh, R. (author) / Seyedein, S.H. (author) / Aboutalebi, M.R. (author)
2009-09-22
6 pages
Article (Journal)
Electronic Resource
English
| British Library Online Contents | 2010
Optimized warm peening of the quenched and tempered steel AISI 4140
| British Library Online Contents | 2002
Residual Stress Depth Distribution after Piezo Peening of Quenched and Tempered AISI 4140
| British Library Online Contents | 2014
Axial fatigue of a gas-nitrided quenched and tempered AISI 4140 steel: effect of nitriding depth
| British Library Online Contents | 2003
| British Library Online Contents | 1997