Corrosion inhibitors based on chitosan-heptanoate modified beidellite
Abstract This study deals with the development of a novel inhibitor based on heptanoate anions encapsulated within chitosan-modified beidellite. Included in coating, this inhibitor ensured efficient protection of metals against wet corrosion via permanent controllable release of the heptanoate inhibitor. The interlayer Na+ ions of beidellite from Agadir basin (Morocco) were exchanged with chitosan cations. The modified beidellite was studied by diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS), thermogravimetry (TG) analysis coupled to mass spectrometry (MS) and, X-ray diffraction (XRD) analysis. The expansion of the interlayer space of beidellite by ≈1.16nm, evidenced by XRD, was consistent with the arrangement of chitosan bilayer. Exceeding positively charged sites of the biopolymer were compensated by heptanoate anions. Electrochemical impedance spectroscopy (EIS) measurements were carried out on galvanized steel immersed in a 3mass% NaCl solution. The measurements revealed improvement of corrosion inhibition by chitosan-heptanoate modified beidellite in comparison with commercially available triphosphate aluminium (TPA) anti corrosion pigments. The improved corrosion inhibition was due to the continuous leaching of hepatanoate anions as inhibitors. However, the barrier properties of coatings containing chitosan-heptanoate modified beidellite were not as high as those of TPA-based coatings, probably due to insufficient dispersion of the modified beidellite particles within the polymeric matrix.
Graphical abstract Display Omitted Highlights ► Chitosan heptanoate modified beidellite as corrosion inhibitor. ► Chitosan heptanoate modified beidellite more efficient than commercial TPA pigments. ► Functionalized natural clay for eco-friendly corrosion inhibition.
Corrosion inhibitors based on chitosan-heptanoate modified beidellite
Abstract This study deals with the development of a novel inhibitor based on heptanoate anions encapsulated within chitosan-modified beidellite. Included in coating, this inhibitor ensured efficient protection of metals against wet corrosion via permanent controllable release of the heptanoate inhibitor. The interlayer Na+ ions of beidellite from Agadir basin (Morocco) were exchanged with chitosan cations. The modified beidellite was studied by diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS), thermogravimetry (TG) analysis coupled to mass spectrometry (MS) and, X-ray diffraction (XRD) analysis. The expansion of the interlayer space of beidellite by ≈1.16nm, evidenced by XRD, was consistent with the arrangement of chitosan bilayer. Exceeding positively charged sites of the biopolymer were compensated by heptanoate anions. Electrochemical impedance spectroscopy (EIS) measurements were carried out on galvanized steel immersed in a 3mass% NaCl solution. The measurements revealed improvement of corrosion inhibition by chitosan-heptanoate modified beidellite in comparison with commercially available triphosphate aluminium (TPA) anti corrosion pigments. The improved corrosion inhibition was due to the continuous leaching of hepatanoate anions as inhibitors. However, the barrier properties of coatings containing chitosan-heptanoate modified beidellite were not as high as those of TPA-based coatings, probably due to insufficient dispersion of the modified beidellite particles within the polymeric matrix.
Graphical abstract Display Omitted Highlights ► Chitosan heptanoate modified beidellite as corrosion inhibitor. ► Chitosan heptanoate modified beidellite more efficient than commercial TPA pigments. ► Functionalized natural clay for eco-friendly corrosion inhibition.
Corrosion inhibitors based on chitosan-heptanoate modified beidellite
Aghzzaf, Ahmed Aït (author) / Rhouta, Benaissa (author) / Steinmetz, Jean (author) / Rocca, Emmanuel (author) / Aranda, Lionel (author) / Khalil, Aziza (author) / Yvon, Jacques (author) / Daoudi, Lahcen (author)
Applied Clay Science ; 65-66 ; 173-178
2012-04-28
6 pages
Article (Journal)
Electronic Resource
English
Beidellite , Chitosan , Heptanoate , Corrosion , Inhibition
Corrosion inhibitors based on chitosan-heptanoate modified beidellite
| Online Contents | 2012
Infrared emission spectroscopy of Al-pillared beidellite
| Online Contents | 1999
| British Library Online Contents | 2014
Hydrothermal synthesis of Na beidellite from coprecipitated gel
| British Library Online Contents | 1996