Microstructure and characterization of hydrothermal synthesis of Al-substituted tobermorite: Fid-Bau Portal

Microstructure and characterization of hydrothermal synthesis of Al-substituted tobermorite

Guo, Xiaolu / Meng, Fanjie / Shi, Huisheng

Highlights•The suitable synthesis condition for tobermorite was 5h in autoclave at 180°C.•Addition of aluminum resulted in an increased interlayer spacing.•The tobermorite with the incorporated of aluminum had a longer mean chain length.•The microstructure of tobermorite with aluminum had larger and more ordered foils.

AbstractTobermorite is an important mineral analog of calcium silicate hydrate (C-S-H), the main phase formed by hydration of Portland cement, due to the structural similarity. As part of a broader study on the effect of aluminum substitution C-S-H, the synthesis and characterization of tobermorite with and without aluminum were conducted. The X-ray diffraction pattern indicated that a suitable synthesis time for tobermorite with or without aluminum was 5 h in an autoclave at 180°C and saturated steam pressure around 1MPa. In both samples the mineral is 11Å-tobermorite. X-ray fluorescence showed that the sample with aluminum had a higher molar ratio of Ca/(Si+Al). Thermogravimetry-differential scanning calorimetry showed the same general changes, loss of free water at 55°C, loss of interlayer water at 187°C, dehydroxylation at 664°C, and conversion to wollastonite at 841°C. With the incorporation of aluminum, 29Si and 27Al magic angle spinning-nuclear magnetic resonance spectra showed aluminum addition increases the mean chain length, Al mainly occupies Q² bridging and Q³ branching sites. Scanning electron micrographs indicated that tobermorite crystals are larger than those of sample without alumina. This work is beneficial for understanding the implication of the use of admixtures containing aluminum in concrete on its micro- and atomic-scale properties.