The invention discloses a manufacturing method of a bonding material for composite floors. The manufacturing method comprises the following steps: (1) mixing 12-18 parts of an acrylate monomer, 4-12 parts of an epoxy resin room temperature curing agent, 6-10 parts of polyethylene glycol diacrylate, 48-54 parts of butyl acrylate, 30-50 parts of methyl acrylate, 2-4 parts of lauryl sodium sulfate and 0.1-0.4 part of ammonium sulfate, and uniformly stirring to obtain a pre-emulsified liquid; (2) mixing water with the pre-emulsified liquid obtained in the step (1), heating, uniformly mixing, and cooling to obtain a reaction liquid; and (3) adding 8-14 parts of rosin and 12-24 parts of epoxy resin into the reaction liquid obtained in the step (2), and uniformly stirring to obtain the final bonding material. According to the bonding material for the composite floors, the adhesiveness of the composite floors can be effectively improved, and the problem that the composite floors are easy to split is solved.
本发明公开了一种复合地板用粘合材料的制作方法，(1)将丙烯酸酯单体12份～18份、环氧树脂室温固化剂4份～12份、聚乙二醇二丙烯酸酯6份～10份、丙烯酸丁酯48份～54份、丙烯酸甲酯30份～50份、十二烷基硫酸钠2份～4份、硫酸铵0.1份～0.4份混合，搅拌均匀，得到预乳化液；(2)将水与步骤(1)获得的预乳化液混合，升温混匀后冷却，得到反应液；(3)向步骤(2)的反应液中加入松香8份～14份、环氧树脂12份～24份，搅拌均匀后获得最终的粘合材料。本发明制作的复合地板用粘合材料，可以有效提高复合地板的粘合性，解决复合地板容易开叉的问题。
The invention discloses a manufacturing method of a bonding material for composite floors. The manufacturing method comprises the following steps: (1) mixing 12-18 parts of an acrylate monomer, 4-12 parts of an epoxy resin room temperature curing agent, 6-10 parts of polyethylene glycol diacrylate, 48-54 parts of butyl acrylate, 30-50 parts of methyl acrylate, 2-4 parts of lauryl sodium sulfate and 0.1-0.4 part of ammonium sulfate, and uniformly stirring to obtain a pre-emulsified liquid; (2) mixing water with the pre-emulsified liquid obtained in the step (1), heating, uniformly mixing, and cooling to obtain a reaction liquid; and (3) adding 8-14 parts of rosin and 12-24 parts of epoxy resin into the reaction liquid obtained in the step (2), and uniformly stirring to obtain the final bonding material. According to the bonding material for the composite floors, the adhesiveness of the composite floors can be effectively improved, and the problem that the composite floors are easy to split is solved.
本发明公开了一种复合地板用粘合材料的制作方法，(1)将丙烯酸酯单体12份～18份、环氧树脂室温固化剂4份～12份、聚乙二醇二丙烯酸酯6份～10份、丙烯酸丁酯48份～54份、丙烯酸甲酯30份～50份、十二烷基硫酸钠2份～4份、硫酸铵0.1份～0.4份混合，搅拌均匀，得到预乳化液；(2)将水与步骤(1)获得的预乳化液混合，升温混匀后冷却，得到反应液；(3)向步骤(2)的反应液中加入松香8份～14份、环氧树脂12份～24份，搅拌均匀后获得最终的粘合材料。本发明制作的复合地板用粘合材料，可以有效提高复合地板的粘合性，解决复合地板容易开叉的问题。
Manufacturing method of bonding material for composite floors
一种复合地板用粘合材料的制作方法
LI JING (author)
2020-04-24
Patent
Electronic Resource
Chinese
Preparation method of bonding material for reinforced composite floors
| European Patent Office | 2020
Preparation method of bonding material for bamboo-wood floors
| European Patent Office | 2020