Process method for preparing compact calcium hexaluminate refractory clinker by one-step method
The invention relates to a process method for preparing a compact calcium hexaluminate refractory clinker by a one-step method. The compact calcium hexaluminate refractory clinker comprises the following components in percentage by weight: 87.96-89.79% of Al2O3, 8.04-8.21% of CaO and 2.00-4.00% of A micro powder, wherein the relative density is 91.30%-94.60%, and the apparent porosity is 2.80%-4.50%; the preparation method comprises the following steps: (1) respectively grinding bauxite, limestone and micro powder A, and mixing; and (2) pressing the mixed material into green pellets, and calcining to obtain clinker. According to the invention, the A micro powder is used as a sintering promoter; in the calcining process, the micro powder A is subjected to solid solution in a calcium hexaluminate phase to form a solid solution, so the sintering activity of the calcium hexaluminate phase is improved, and the growth of the calcium hexaluminate phase is promoted, so that the compact calciumhexaluminate refractory clinker can be obtained under the conditions of lower calcination temperature and shorter heat preservation time, the production energy consumption is effectively reduced, theproduction efficiency is improved, and the energy conservation and emission reduction are promoted.
一种一步法制备致密六铝酸钙耐火熟料的工艺方法，其成分按重量百分比含AlO87.96~89.79%，CaO 8.04~8.21%，A微粉2.00~4.00%；相对密度为91.30~94.60%，显气孔率为2.80~4.50%；制备方法为：（1）将铝矾土、石灰石和A微粉分别磨细后混合；（2）将混合物料压制成生球，然后进行煅烧制成熟料。本发明采用A微粉作为促烧结剂，在煅烧过程A微粉固溶到六铝酸钙相中形成固溶体，从而提高了六铝酸钙相的烧结活性，促进六铝酸钙相的长大，从而可在较低的煅烧温度和较短的保温时间条件下获得致密六铝酸钙耐火熟料，有效降低了生产能耗，提高了生产效率，促进了节能减排。
Process method for preparing compact calcium hexaluminate refractory clinker by one-step method
The invention relates to a process method for preparing a compact calcium hexaluminate refractory clinker by a one-step method. The compact calcium hexaluminate refractory clinker comprises the following components in percentage by weight: 87.96-89.79% of Al2O3, 8.04-8.21% of CaO and 2.00-4.00% of A micro powder, wherein the relative density is 91.30%-94.60%, and the apparent porosity is 2.80%-4.50%; the preparation method comprises the following steps: (1) respectively grinding bauxite, limestone and micro powder A, and mixing; and (2) pressing the mixed material into green pellets, and calcining to obtain clinker. According to the invention, the A micro powder is used as a sintering promoter; in the calcining process, the micro powder A is subjected to solid solution in a calcium hexaluminate phase to form a solid solution, so the sintering activity of the calcium hexaluminate phase is improved, and the growth of the calcium hexaluminate phase is promoted, so that the compact calciumhexaluminate refractory clinker can be obtained under the conditions of lower calcination temperature and shorter heat preservation time, the production energy consumption is effectively reduced, theproduction efficiency is improved, and the energy conservation and emission reduction are promoted.
一种一步法制备致密六铝酸钙耐火熟料的工艺方法，其成分按重量百分比含AlO87.96~89.79%，CaO 8.04~8.21%，A微粉2.00~4.00%；相对密度为91.30~94.60%，显气孔率为2.80~4.50%；制备方法为：（1）将铝矾土、石灰石和A微粉分别磨细后混合；（2）将混合物料压制成生球，然后进行煅烧制成熟料。本发明采用A微粉作为促烧结剂，在煅烧过程A微粉固溶到六铝酸钙相中形成固溶体，从而提高了六铝酸钙相的烧结活性，促进六铝酸钙相的长大，从而可在较低的煅烧温度和较短的保温时间条件下获得致密六铝酸钙耐火熟料，有效降低了生产能耗，提高了生产效率，促进了节能减排。
Process method for preparing compact calcium hexaluminate refractory clinker by one-step method
一种一步法制备致密六铝酸钙耐火熟料的工艺方法
YIN XUELIANG (author) / MA HELI (author) / DU CHENGWU (author) / GONG CHANGWEI (author) / LI LIYING (author) / PENG KEWU (author) / HAN TINGQUAN (author) / DING HONGHAI (author) / YIN XUEDONG (author) / ZHANG BO (author)
2020-05-05
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Process method for preparing compact calcium hexaluminate refractory clinker by one-step method
| European Patent Office | 2021
Process method for preparing compact calcium dialuminate refractory clinker by one-step method
| European Patent Office | 2020
Technological method for preparing compact calcium dialuminate refractory clinker by one-step method
| European Patent Office | 2021
Preparation method of compact calcium hexaluminate ceramic
| European Patent Office | 2023
High-purity compact calcium hexaluminate series refractory material and preparation method thereof
| European Patent Office | 2022