High-strength unfired ceramsite and preparation method thereof
The invention relates to the technical field of building materials, in particular to high-strength unfired ceramsite and a preparation method thereof. The high-strength unfired ceramsite provided by the invention comprises the following raw materials in parts by weight: 50-70 parts of engineering spoil, 15 to 35 parts of fly ash, 5 to 10 parts of cement, 1-2 parts of a reinforcing agent, 5-10 parts of a solid excitant, 1-8 parts of a liquid excitant and 20-30 parts of water. According to the invention, the engineering spoil is used as a base material, the cement and the fly ash are used as cementing materials, the reinforcing agent is used as a reinforcing material, and under the excitation of an excitant, the high-strength unfired ceramsite is obtained through cooperation of all the raw materials with specific usage amounts.
本发明涉及建筑材料技术领域，具体涉及一种高强免烧陶粒及其制备方法。本发明提供的高强免烧陶粒，包括以下重量份数的制备原料：工程弃土50～70份；粉煤灰15～35份；水泥5～10份；增强剂1～2份；固态激发剂5～10份；液态激发剂1～8份；水20～30份。本发明以工程弃土为基材，以水泥和粉煤灰作为胶凝材料，以增强剂作为加强材料，在激发剂的激发下，配合各原料的用量得到了具有较高强度的免烧陶粒。
High-strength unfired ceramsite and preparation method thereof
The invention relates to the technical field of building materials, in particular to high-strength unfired ceramsite and a preparation method thereof. The high-strength unfired ceramsite provided by the invention comprises the following raw materials in parts by weight: 50-70 parts of engineering spoil, 15 to 35 parts of fly ash, 5 to 10 parts of cement, 1-2 parts of a reinforcing agent, 5-10 parts of a solid excitant, 1-8 parts of a liquid excitant and 20-30 parts of water. According to the invention, the engineering spoil is used as a base material, the cement and the fly ash are used as cementing materials, the reinforcing agent is used as a reinforcing material, and under the excitation of an excitant, the high-strength unfired ceramsite is obtained through cooperation of all the raw materials with specific usage amounts.
本发明涉及建筑材料技术领域，具体涉及一种高强免烧陶粒及其制备方法。本发明提供的高强免烧陶粒，包括以下重量份数的制备原料：工程弃土50～70份；粉煤灰15～35份；水泥5～10份；增强剂1～2份；固态激发剂5～10份；液态激发剂1～8份；水20～30份。本发明以工程弃土为基材，以水泥和粉煤灰作为胶凝材料，以增强剂作为加强材料，在激发剂的激发下，配合各原料的用量得到了具有较高强度的免烧陶粒。
High-strength unfired ceramsite and preparation method thereof
一种高强免烧陶粒及其制备方法
GUAN YU (author) / XIN XIAOTING (author) / OU XIAOFAN (author) / YU SHAN (author) / HU JUNPAN (author) / XIN JIBAO (author)
2020-05-19
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Lightweight high-strength unfired ceramsite and preparation method thereof
| European Patent Office | 2024
Unfired ceramsite based on ditch bottom mud and preparation method of unfired ceramsite
| European Patent Office | 2022