Light-transmitting concrete and manufacturing method thereof
The invention provides light-transmitting concrete and a manufacturing method thereof. The light-transmitting concrete comprises a cement base and a light guide material, the light guide material is buried in a cement base material matrix in a certain spatial permutation and combination mode, and the cement base comprises water, Portland cement, sulphoaluminate cement, fly ash, anhydrous sodium sulfate, a polycarboxylate superplasticizer, medium sand and redispersible latex powder; the weight parts of all the components are as follows: 170 parts of water, 361-369 parts of Portland cement, 13-18 parts of sulphoaluminate cement, 63-65 parts of fly ash, 6-7 parts of anhydrous sodium sulfate, 2.9 parts of a polycarboxylate superplasticizer, 1350 parts of medium sand and 6.3 parts of redispersible latex powder. The weight ratio of the sulphoaluminate cement to the anhydrous sodium sulfate is (1.3-2.6):1, and the weight ratio of the mixture of the Portland cement, the fly ash, the sulphoaluminate cement and the anhydrous sodium sulfate to the redispersible latex powder is 1000:14. The concrete disclosed by the invention is wide in raw material source, good in working performance, strongin binding power, low in cost and good in anti-cracking performance, and can be used for integrally forming a light-transmitting concrete large plate.
本发明提供一种透光混凝土及其制作方法,透光混凝土包括水泥基及导光材料,导光材料以一定空间排列组合方式埋入水泥基材料基体中,水泥基包括水、硅酸盐水泥、硫铝酸盐水泥、粉煤灰、无水硫酸钠、聚羧酸减水剂、中砂及可再分散乳胶粉;各组分的重量份如下:水170份、硅酸盐水泥361‑369份、硫铝酸盐水泥13‑18份、粉煤灰63‑65份、无水硫酸钠6‑7份、聚羧酸减水剂2.9份、中砂1350份、可再分散乳胶粉6.3份,硫铝酸盐水泥与无水硫酸钠的重量比为(1.3‑2.6):1,硅酸盐水泥、粉煤灰、硫铝酸盐水泥、无水硫酸钠的混合物与可再分散乳胶粉的重量比为1000:14。本发明的混凝土原料来源广泛,工作性能好,粘结力强,成本低,且具备良好的抗裂性能,可整体成型透光混凝土大板。
Light-transmitting concrete and manufacturing method thereof
The invention provides light-transmitting concrete and a manufacturing method thereof. The light-transmitting concrete comprises a cement base and a light guide material, the light guide material is buried in a cement base material matrix in a certain spatial permutation and combination mode, and the cement base comprises water, Portland cement, sulphoaluminate cement, fly ash, anhydrous sodium sulfate, a polycarboxylate superplasticizer, medium sand and redispersible latex powder; the weight parts of all the components are as follows: 170 parts of water, 361-369 parts of Portland cement, 13-18 parts of sulphoaluminate cement, 63-65 parts of fly ash, 6-7 parts of anhydrous sodium sulfate, 2.9 parts of a polycarboxylate superplasticizer, 1350 parts of medium sand and 6.3 parts of redispersible latex powder. The weight ratio of the sulphoaluminate cement to the anhydrous sodium sulfate is (1.3-2.6):1, and the weight ratio of the mixture of the Portland cement, the fly ash, the sulphoaluminate cement and the anhydrous sodium sulfate to the redispersible latex powder is 1000:14. The concrete disclosed by the invention is wide in raw material source, good in working performance, strongin binding power, low in cost and good in anti-cracking performance, and can be used for integrally forming a light-transmitting concrete large plate.
本发明提供一种透光混凝土及其制作方法,透光混凝土包括水泥基及导光材料,导光材料以一定空间排列组合方式埋入水泥基材料基体中,水泥基包括水、硅酸盐水泥、硫铝酸盐水泥、粉煤灰、无水硫酸钠、聚羧酸减水剂、中砂及可再分散乳胶粉;各组分的重量份如下:水170份、硅酸盐水泥361‑369份、硫铝酸盐水泥13‑18份、粉煤灰63‑65份、无水硫酸钠6‑7份、聚羧酸减水剂2.9份、中砂1350份、可再分散乳胶粉6.3份,硫铝酸盐水泥与无水硫酸钠的重量比为(1.3‑2.6):1,硅酸盐水泥、粉煤灰、硫铝酸盐水泥、无水硫酸钠的混合物与可再分散乳胶粉的重量比为1000:14。本发明的混凝土原料来源广泛,工作性能好,粘结力强,成本低,且具备良好的抗裂性能,可整体成型透光混凝土大板。
Light-transmitting concrete and manufacturing method thereof
一种透光混凝土及其制作方法
WANG YU (author) / ZHU MINTAO (author) / ZHOU QIANG (author) / LIU LONG (author) / FAN SHENGHUA (author)
2020-05-29
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Light transmitting concrete block using photocatalyst and manufacturing method thereof
European Patent Office | 2020
|Light transmitting concrete block using photocatalyst and manufacturing method thereof
European Patent Office | 2020
Light-transmitting concrete and preparation method thereof
European Patent Office | 2024
|Manufacturing method of modeling light-transmitting concrete
European Patent Office | 2020
|Light-transmitting concrete and preparation method thereof
European Patent Office | 2023
|