The invention provides a cinnabar red ceramic colored drawing process, which comprises the following steps: adding rust red into finely ground cinnabar, and blending the mixture with camphor oil to obtain a cinnabar red pigment for later use; drawing a pattern outline on a ceramic white body sintered at high temperature, bottoming a green body with glass white, applying the prepared cinnabar red pigment on the glass white layer, and performing, according to requirement, flat filling or wash-dyeing; and putting the ceramic product into a kiln, and baking the ceramic product at 220-280 DEG C toobtain the cinnabar red ceramic product. The cinnabar prepared by the process is bright red in color, thick, luxurious and textured in color and luster, and not liable to fade. The process is particularly suitable for colored drawing decoration of the display art porcelain.
本发明提供一种朱砂红彩陶瓷彩绘工艺，包括：将铁锈红加入细磨后的朱砂，用樟脑油调制成朱砂红色料备用；在高温烧成的陶瓷白胎上勾画出图案轮廓，用玻璃白打底，再将制好的朱砂红色料施于这层玻璃白之上，根据需要平填或洗染；将陶瓷制品入窑经220℃～280℃烘烤获得朱砂红彩陶瓷制品。由该工艺制作的朱砂红彩呈色鲜红，色泽厚重华贵有质感、不易褪色。该工艺尤其适用于陈设艺术瓷的彩绘装饰。
The invention provides a cinnabar red ceramic colored drawing process, which comprises the following steps: adding rust red into finely ground cinnabar, and blending the mixture with camphor oil to obtain a cinnabar red pigment for later use; drawing a pattern outline on a ceramic white body sintered at high temperature, bottoming a green body with glass white, applying the prepared cinnabar red pigment on the glass white layer, and performing, according to requirement, flat filling or wash-dyeing; and putting the ceramic product into a kiln, and baking the ceramic product at 220-280 DEG C toobtain the cinnabar red ceramic product. The cinnabar prepared by the process is bright red in color, thick, luxurious and textured in color and luster, and not liable to fade. The process is particularly suitable for colored drawing decoration of the display art porcelain.
本发明提供一种朱砂红彩陶瓷彩绘工艺，包括：将铁锈红加入细磨后的朱砂，用樟脑油调制成朱砂红色料备用；在高温烧成的陶瓷白胎上勾画出图案轮廓，用玻璃白打底，再将制好的朱砂红色料施于这层玻璃白之上，根据需要平填或洗染；将陶瓷制品入窑经220℃～280℃烘烤获得朱砂红彩陶瓷制品。由该工艺制作的朱砂红彩呈色鲜红，色泽厚重华贵有质感、不易褪色。该工艺尤其适用于陈设艺术瓷的彩绘装饰。
Ceramic firing method using the cinnabar glaze composition
European Patent Office | 2018
Ceramic firing method using the cinnabar glaze composition
| European Patent Office | 2017
GLAZE COMPOSITION FOR CINNABAR CHINA AND METHOD OF MANUFACTURING CINNABAR CHINA BY USING THE SAME
European Patent Office | 2017