Suet-white-jade-like white ceramic product and preparation method thereof
The invention discloses a suet-white-jade-like white ceramic product and a preparation method thereof, and belongs to the technical field of ceramic products. The suet-white-jade-like white ceramic product comprises a billet material and a glaze material, wherein the billet material is prepared from the following raw materials in parts by weight: 62 parts of kaolin, 13 parts of quartz, 37 parts oflithium chinastone, 23 parts of potassium feldspar, 2 parts of talc, 19 parts of wollastonite, 14 parts of abrazite, 10 parts of vermiculite, 8 parts of calcium silicate, 8 parts of barium sulfate and 6 parts of sepiolite, and the glaze material is prepared from the following raw materials in parts by weight: 48 parts of potassium feldspar, 14 parts of shell powder, 27 parts of quartz, 29 parts of barium carbonate, 13 parts of zirconium silicate, 2 parts of titanium oxide and 5 parts of talc. The preparation method comprises the following main steps: S1, burdening; S2, billet drawing; S3, biscuiting; S4, glazing; and S5, firing. The ceramic product prepared by the method has the characteristics of being as white as jade and excellent in mechanical property.
本发明公开了一种如脂玉白陶瓷制品及其制备方法，属于陶瓷制品技术领域。所述如脂玉白陶瓷制品包括坯料和釉料，所述坯料由以下重量份的原料组成：高岭土62份、石英13份、锂瓷石37份、钾长石23份、滑石2份、硅灰石19份、水钙沸石14份、蛭石10份、硅酸钙8份、硫酸钡8份、海泡石6份；所述釉料由以下重量份原料组成：钾长石48份、贝壳粉末14份、石英27份、碳酸钡29份、硅酸锆13份、氧化钛2份、滑石5份。本发明的制备方法主要步骤为：S1配料、S2拉坯、S3素烧、S4上釉、S5烧成。本发明制备的陶瓷制品具有润白如玉以及机械性能优异的特点。
Suet-white-jade-like white ceramic product and preparation method thereof
The invention discloses a suet-white-jade-like white ceramic product and a preparation method thereof, and belongs to the technical field of ceramic products. The suet-white-jade-like white ceramic product comprises a billet material and a glaze material, wherein the billet material is prepared from the following raw materials in parts by weight: 62 parts of kaolin, 13 parts of quartz, 37 parts oflithium chinastone, 23 parts of potassium feldspar, 2 parts of talc, 19 parts of wollastonite, 14 parts of abrazite, 10 parts of vermiculite, 8 parts of calcium silicate, 8 parts of barium sulfate and 6 parts of sepiolite, and the glaze material is prepared from the following raw materials in parts by weight: 48 parts of potassium feldspar, 14 parts of shell powder, 27 parts of quartz, 29 parts of barium carbonate, 13 parts of zirconium silicate, 2 parts of titanium oxide and 5 parts of talc. The preparation method comprises the following main steps: S1, burdening; S2, billet drawing; S3, biscuiting; S4, glazing; and S5, firing. The ceramic product prepared by the method has the characteristics of being as white as jade and excellent in mechanical property.
本发明公开了一种如脂玉白陶瓷制品及其制备方法，属于陶瓷制品技术领域。所述如脂玉白陶瓷制品包括坯料和釉料，所述坯料由以下重量份的原料组成：高岭土62份、石英13份、锂瓷石37份、钾长石23份、滑石2份、硅灰石19份、水钙沸石14份、蛭石10份、硅酸钙8份、硫酸钡8份、海泡石6份；所述釉料由以下重量份原料组成：钾长石48份、贝壳粉末14份、石英27份、碳酸钡29份、硅酸锆13份、氧化钛2份、滑石5份。本发明的制备方法主要步骤为：S1配料、S2拉坯、S3素烧、S4上釉、S5烧成。本发明制备的陶瓷制品具有润白如玉以及机械性能优异的特点。
Suet-white-jade-like white ceramic product and preparation method thereof
一种如脂玉白陶瓷制品及其制备方法
ZENG XINYU (author)
2020-06-19
Patent
Electronic Resource
Chinese
Transparent white jade ceramic vase and production process thereof
| European Patent Office | 2024
| European Patent Office | 2023
| European Patent Office | 2023
Ultra-white light-transmitting jade ceramic tile and processing method thereof
| European Patent Office | 2022