Preparation method of matt reaction three-color glaze
The invention discloses a preparation method of a matt reaction three-color glaze. The method comprises the following steps of S1, washing a blank with water, glazing an inner glaze, smearing an opening and drying, S2, coating the blank with outer glaze and airing for 3-5 min, S3, brushing the blank coated with the outer glaze with three reaction glazes according to design requirements, and then airing for 6-8 hours, and S4, firing the blank brushed with the reaction glaze in an environment of 1190-1250 DEG C to obtain a finished product. The concentrations of the outer glaze and the three reaction glazes are controlled to be 38-42 Baume degrees; and specific gravity is controlled to be 1.2-1.3. The glaze surface prepared by the method is fine, smooth and saturated, the patterns of the reaction glaze surface are uniform, the color development is consistent, and the glaze surface is easy to clean and not easy to dirty.
本发明公开了一种无光反应三色釉的制备方法，方法的步骤中含有：S1：坯件洗水，上内釉，抹口，烘干；S2：坯件上上好外釉，并晾干3‑5分钟；S3：上好外釉的坯件按照设计要求刷三种反应釉，然后晾干6～8小时；S4：刷反应釉后的坯件在1190℃～1250℃的环境下烧成得成品；其中，外釉和三种反应釉的浓度控制在38～42波美度；比重控制在1.2～1.3。通过该方法制备得到的釉釉面细腻，饱和，反应釉面花纹均匀，发色一致，釉面易于清洗，不易脏。
Preparation method of matt reaction three-color glaze
The invention discloses a preparation method of a matt reaction three-color glaze. The method comprises the following steps of S1, washing a blank with water, glazing an inner glaze, smearing an opening and drying, S2, coating the blank with outer glaze and airing for 3-5 min, S3, brushing the blank coated with the outer glaze with three reaction glazes according to design requirements, and then airing for 6-8 hours, and S4, firing the blank brushed with the reaction glaze in an environment of 1190-1250 DEG C to obtain a finished product. The concentrations of the outer glaze and the three reaction glazes are controlled to be 38-42 Baume degrees; and specific gravity is controlled to be 1.2-1.3. The glaze surface prepared by the method is fine, smooth and saturated, the patterns of the reaction glaze surface are uniform, the color development is consistent, and the glaze surface is easy to clean and not easy to dirty.
本发明公开了一种无光反应三色釉的制备方法，方法的步骤中含有：S1：坯件洗水，上内釉，抹口，烘干；S2：坯件上上好外釉，并晾干3‑5分钟；S3：上好外釉的坯件按照设计要求刷三种反应釉，然后晾干6～8小时；S4：刷反应釉后的坯件在1190℃～1250℃的环境下烧成得成品；其中，外釉和三种反应釉的浓度控制在38～42波美度；比重控制在1.2～1.3。通过该方法制备得到的釉釉面细腻，饱和，反应釉面花纹均匀，发色一致，釉面易于清洗，不易脏。
Preparation method of matt reaction three-color glaze
一种无光反应三色釉的制备方法
PAN JUNYUN (author)
2020-07-07
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Matt double-layer reaction glaze brushed decoration and preparation method
| European Patent Office | 2021
Waste porcelain powder doped matt color glaze, ceramic product and preparation method
| European Patent Office | 2021
| European Patent Office | 2021