Novel resin type artificial stone and preparation method thereof
The invention discloses a novel resin type artificial stone and a preparation method thereof. The novel resin type artificial stone is composed of an aggregate, a filler, steel wires, a cementing agent and an ultraviolet absorbent. The aggregate is prepared from the following basalt stones of intermittent grades in parts by weight: 18 to 28 parts of particles with particle sizes ranging from 20 mmto 23 mm, 16 to 23 parts of particles with particle sizes ranging from 15 mm to 18 mm, 12 to 17 parts of particles with particle sizes ranging from 10 mm to 13 mm, 9 to 13 parts of particles with particle sizes ranging from 5 mm to 9 mm, 5 to 7 parts of particles with particle sizes ranging from 2 mm to 4 mm and 5 to 8 parts of particles with particle sizes ranging from 1 mm to 2 mm. The filler is fly ash, quartz powder and calcium carbonate powder. The cementing agent is composed of, in parts by weight, 6 to 12 parts of epoxy resin 0683A and 2 to 4 parts of an epoxy curing agent 0683B. The prepared resin type artificial stone is high in strength and hardness, the phenomena of cracking and breaking do not occur, and the application range of the resin type artificial stone is wider.
本发明公开了一种新型树脂型人造石及其制备方法，由集料、填料、钢丝、胶结剂和紫外吸收剂组成，集料采用玄武岩石子按断续级的重量份是：粒度20‑23mm范围内的颗粒为18‑28，粒度15‑18mm范围内的颗粒为16‑23，粒度10‑13mm范围内的颗粒为12‑17份，粒度5‑9mm范围内的颗粒为9‑13份，粒度2‑4mm范围内的颗粒为5‑9份，粒度1‑2mm范围内的颗粒为5‑8份；填料采用粉煤灰、石英粉和碳酸钙粉，粉煤灰；胶结剂是由重量份是0683A环氧树脂6‑12份和0683B环氧固化剂2‑4份组成；制得的树脂型人造石的强度、硬度高，不出现开裂断裂的现象，使其能够应用的范围更广。
Novel resin type artificial stone and preparation method thereof
The invention discloses a novel resin type artificial stone and a preparation method thereof. The novel resin type artificial stone is composed of an aggregate, a filler, steel wires, a cementing agent and an ultraviolet absorbent. The aggregate is prepared from the following basalt stones of intermittent grades in parts by weight: 18 to 28 parts of particles with particle sizes ranging from 20 mmto 23 mm, 16 to 23 parts of particles with particle sizes ranging from 15 mm to 18 mm, 12 to 17 parts of particles with particle sizes ranging from 10 mm to 13 mm, 9 to 13 parts of particles with particle sizes ranging from 5 mm to 9 mm, 5 to 7 parts of particles with particle sizes ranging from 2 mm to 4 mm and 5 to 8 parts of particles with particle sizes ranging from 1 mm to 2 mm. The filler is fly ash, quartz powder and calcium carbonate powder. The cementing agent is composed of, in parts by weight, 6 to 12 parts of epoxy resin 0683A and 2 to 4 parts of an epoxy curing agent 0683B. The prepared resin type artificial stone is high in strength and hardness, the phenomena of cracking and breaking do not occur, and the application range of the resin type artificial stone is wider.
本发明公开了一种新型树脂型人造石及其制备方法，由集料、填料、钢丝、胶结剂和紫外吸收剂组成，集料采用玄武岩石子按断续级的重量份是：粒度20‑23mm范围内的颗粒为18‑28，粒度15‑18mm范围内的颗粒为16‑23，粒度10‑13mm范围内的颗粒为12‑17份，粒度5‑9mm范围内的颗粒为9‑13份，粒度2‑4mm范围内的颗粒为5‑9份，粒度1‑2mm范围内的颗粒为5‑8份；填料采用粉煤灰、石英粉和碳酸钙粉，粉煤灰；胶结剂是由重量份是0683A环氧树脂6‑12份和0683B环氧固化剂2‑4份组成；制得的树脂型人造石的强度、硬度高，不出现开裂断裂的现象，使其能够应用的范围更广。
Novel resin type artificial stone and preparation method thereof
一种新型树脂型人造石及其制备方法
JIA XINJIE (author) / SHI ZEBO (author) / ZHANG XINLI (author) / DU YINGFEI (author) / FU SISHUN (author) / WU LONGHAI (author) / WANG XIAOJUAN (author)
2020-07-28
Patent
Electronic Resource
Chinese
Resin type artificial stone and production process thereof
| European Patent Office | 2021
Coal gangue/PVC resin artificial stone plate and preparation method thereof
| European Patent Office | 2020
Novel deodorizing antibacterial artificial stone and preparation method thereof
| European Patent Office | 2021