The invention discloses a fluorescent permeable concrete pavement brick and a preparation method thereof, and belongs to the technical field of concrete. The invention is characterized in that the brick is prepared from the following raw materials in parts by weight: 50 to 70 parts of machine-made sand; 12-24 parts of cement, 8-10 parts of steel slag, 1-2 parts of a steel slag modifier; 0.3 to 0.8part of a water reducing agent; 1.3-1.5 parts of pigment, 3.5-6 parts of water, 0.9-1.1 parts of urea, 1-2 parts of an organic modifier, 1-3 parts of a fluorescent material, 2-4 parts of a fluorescent curing agent, 1.3-2 parts of a fluorescent curing agent, 3.5-6 parts of water, 0.9-1.1 parts of urea, 1-2 parts of an organic modifier and 1.1-1.7 parts of a fluorescent material treating agent. Thefluorescent multicolor permeable concrete pavement brick is high in wear resistance and good in strength and durability, and can absorb solar energy in the daytime and release and emit cold light invarious shapes at night.
一种荧光的透水混凝土路面砖及其制备方法，属于混凝土技术领域。其特征在于，是由以下重量份的原料制得的：机制砂50‑70份，水泥12‑24份，钢渣8‑10份，钢渣改性剂1‑2份，减水剂0.3‑0.8份，颜料1.3‑1.5份，水3.5‑6份，尿素0.9‑1.1份，有机改性剂1‑2份，荧光材料1‑3份，荧光固剂2‑4份，荧光固剂理剂1.3‑2份，水3.5‑6份，尿素0.9‑1.1份，有机改性剂1‑2份，荧光材料处理剂1.1‑1.7。本发明的荧光多色透水混凝土路面砖的耐磨性高、强度和耐久性好，其次可以白天吸收太阳能，晚上释放，发出各种形状的冷光。
The invention discloses a fluorescent permeable concrete pavement brick and a preparation method thereof, and belongs to the technical field of concrete. The invention is characterized in that the brick is prepared from the following raw materials in parts by weight: 50 to 70 parts of machine-made sand; 12-24 parts of cement, 8-10 parts of steel slag, 1-2 parts of a steel slag modifier; 0.3 to 0.8part of a water reducing agent; 1.3-1.5 parts of pigment, 3.5-6 parts of water, 0.9-1.1 parts of urea, 1-2 parts of an organic modifier, 1-3 parts of a fluorescent material, 2-4 parts of a fluorescent curing agent, 1.3-2 parts of a fluorescent curing agent, 3.5-6 parts of water, 0.9-1.1 parts of urea, 1-2 parts of an organic modifier and 1.1-1.7 parts of a fluorescent material treating agent. Thefluorescent multicolor permeable concrete pavement brick is high in wear resistance and good in strength and durability, and can absorb solar energy in the daytime and release and emit cold light invarious shapes at night.
一种荧光的透水混凝土路面砖及其制备方法，属于混凝土技术领域。其特征在于，是由以下重量份的原料制得的：机制砂50‑70份，水泥12‑24份，钢渣8‑10份，钢渣改性剂1‑2份，减水剂0.3‑0.8份，颜料1.3‑1.5份，水3.5‑6份，尿素0.9‑1.1份，有机改性剂1‑2份，荧光材料1‑3份，荧光固剂2‑4份，荧光固剂理剂1.3‑2份，水3.5‑6份，尿素0.9‑1.1份，有机改性剂1‑2份，荧光材料处理剂1.1‑1.7。本发明的荧光多色透水混凝土路面砖的耐磨性高、强度和耐久性好，其次可以白天吸收太阳能，晚上释放，发出各种形状的冷光。
Fluorescent multicolor permeable concrete pavement brick and preparation method thereof
一种荧光多色透水混凝土路面砖及其制备方法
LI YANLIN (author)
2020-08-25
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
/
E01C
Bau von Straßen, Sportplätzen oder dgl., Decken dafür
,
CONSTRUCTION OF, OR SURFACES FOR, ROADS, SPORTS GROUNDS, OR THE LIKE
/
E01F
ADDITIONAL WORK, SUCH AS EQUIPPING ROADS OR THE CONSTRUCTION OF PLATFORMS, HELICOPTER LANDING STAGES, SIGNS, SNOW FENCES, OR THE LIKE
,
Zusätzliche Baumaßnahmen, wie die Ausstattung von Straßen oder die bauliche Ausbildung von Bahnsteigen, Landeplätzen für Hubschrauber, Wegweisern, Schneezäunen oder dgl.
| European Patent Office | 2015
Pavement water permeable brick and preparation method thereof
| European Patent Office | 2021