The invention belongs to the field of building materials and relates to luminescent concrete. The luminescent concrete is prepared from the following raw materials in parts by weight: 30-40 parts of cement, 15-20 parts of water, 2-4 parts of a concrete curing agent, 4-8 parts of fluorescent powder, 0.5-1 part of a leveling agent, 4-6 parts of silicon carbide, 6-10 parts of emery powder, 10-15 parts of glass fibers and 20-30 parts of stones. By adding the concrete curing agent, rapid curing of concrete can be achieved, a concrete curing agent material formula is provided, and the concrete curing agent can be widely applied to luminescent concrete and is suitable for application and promotion, by adding silicon carbide, glass fibers, stones and other materials, the strength of the concrete after solidification can be greatly enhanced, so that the concrete can be suitable for places with high strength requirements, by adding the leveling agent, the self-flowing property is good when the concrete is laid on a plane, a leveling agent material formula is provided, the concrete leveling agent can be widely applied to the concrete, and the leveling property of the concrete is improved.
本发明属于建筑材料领域，具体涉及一种发光混凝土，由包括如下重量份的原料制备而成：水泥30‑40份，水15‑20份，混凝土固化剂2‑4份，荧光粉4‑8份，流平剂0.5‑1份，碳化硅4‑6份，刚玉粉6‑10份，玻璃纤维10‑15份，石子20‑30份。本发明通过添加混凝土固化剂，可使得混凝土实现快速固化，且提供了混凝土固化剂材料配方，可广泛适用于发光混凝土中，适宜进行推广使用；通过添加碳化硅、玻璃纤维和石子等材料，可使得混凝土凝固后强度得到大幅增强，从而使得混凝土可适用于高强度需求的场所；通过添加流平剂，可使得混凝土铺设于平面时自流性好，且提供了流平剂材料配方，可广泛应用于混凝土中，提高混凝土的流平性能。
The invention belongs to the field of building materials and relates to luminescent concrete. The luminescent concrete is prepared from the following raw materials in parts by weight: 30-40 parts of cement, 15-20 parts of water, 2-4 parts of a concrete curing agent, 4-8 parts of fluorescent powder, 0.5-1 part of a leveling agent, 4-6 parts of silicon carbide, 6-10 parts of emery powder, 10-15 parts of glass fibers and 20-30 parts of stones. By adding the concrete curing agent, rapid curing of concrete can be achieved, a concrete curing agent material formula is provided, and the concrete curing agent can be widely applied to luminescent concrete and is suitable for application and promotion, by adding silicon carbide, glass fibers, stones and other materials, the strength of the concrete after solidification can be greatly enhanced, so that the concrete can be suitable for places with high strength requirements, by adding the leveling agent, the self-flowing property is good when the concrete is laid on a plane, a leveling agent material formula is provided, the concrete leveling agent can be widely applied to the concrete, and the leveling property of the concrete is improved.
本发明属于建筑材料领域，具体涉及一种发光混凝土，由包括如下重量份的原料制备而成：水泥30‑40份，水15‑20份，混凝土固化剂2‑4份，荧光粉4‑8份，流平剂0.5‑1份，碳化硅4‑6份，刚玉粉6‑10份，玻璃纤维10‑15份，石子20‑30份。本发明通过添加混凝土固化剂，可使得混凝土实现快速固化，且提供了混凝土固化剂材料配方，可广泛适用于发光混凝土中，适宜进行推广使用；通过添加碳化硅、玻璃纤维和石子等材料，可使得混凝土凝固后强度得到大幅增强，从而使得混凝土可适用于高强度需求的场所；通过添加流平剂，可使得混凝土铺设于平面时自流性好，且提供了流平剂材料配方，可广泛应用于混凝土中，提高混凝土的流平性能。
Luminescent concrete
一种发光混凝土
LI XIAOXIN (author)
2020-10-30
Patent
Electronic Resource
Chinese