Foamed ceramic terrazzo composite board and preparation method thereof
The invention provides a foamed ceramic terrazzo composite board and a preparation method thereof. The preparation method comprises the following steps: putting 40% of iron tailing powder, 40% of perlite tailings, 19.6% of kaolin and 0.4% of a foaming agent into a ball mill; adding water and high-aluminum grinding balls according to a weight ratio of the balls to powder to water of 1.6: 1.0: 0.6,then adding sodium tripolyphosphate accounting for 0.5% of the total weight of the powder, and conducting ball milling for 6 h; putting a mixture for foamed ceramic into a refractory mold; putting therefractory mold on a kiln car table board of a tunnel kiln or a roller bar of a roller kiln, conducting firing at a high temperature of 1180 DEG C for 0.5 hour, and carrying out quick cooling to roomtemperature; pouring cement, mineral pigment accounting for 3%-6% of the weight of the cement and stone particles into a terrazzo machine for mixing; and placing sealing partition plates on the periphery of a foamed ceramic partition plate, and flatly laying terrazzo materials on the surface of the foamed ceramic partition plate. The foamed ceramic terrazzo composite board is low in manufacturingcost and good in fireproof and waterproof performance.
本发明提供一种发泡陶瓷水磨石复合板及其制备方法，其中，制备方法如下：将40%铁尾矿粉料，40%珍珠岩尾矿，19.6%高岭土，以及0.4%发泡剂放入球磨机内；按照球：粉料：水为1.6：1.0：0.6的重量比加入水和高铝研磨球，再加入0.5%粉料总重的三聚磷酸钠球磨6h；将发泡陶瓷用混合料放入耐火模具内；将耐火模具放在隧道窑的窑车台面或辊道窑的辊棒上，经过1180°高温烧制0.5h后，快速降温至室温；往水磨石机内倒入水泥、3%～6%水泥重量的矿物颜料、以及石粒进行拌和；在发泡陶瓷隔墙板的四周放置密封隔板，将水磨石料平铺在发泡陶瓷隔墙板的表面。本发明的发泡陶瓷水磨石复合板造价低、防火、防水性能好。
Foamed ceramic terrazzo composite board and preparation method thereof
The invention provides a foamed ceramic terrazzo composite board and a preparation method thereof. The preparation method comprises the following steps: putting 40% of iron tailing powder, 40% of perlite tailings, 19.6% of kaolin and 0.4% of a foaming agent into a ball mill; adding water and high-aluminum grinding balls according to a weight ratio of the balls to powder to water of 1.6: 1.0: 0.6,then adding sodium tripolyphosphate accounting for 0.5% of the total weight of the powder, and conducting ball milling for 6 h; putting a mixture for foamed ceramic into a refractory mold; putting therefractory mold on a kiln car table board of a tunnel kiln or a roller bar of a roller kiln, conducting firing at a high temperature of 1180 DEG C for 0.5 hour, and carrying out quick cooling to roomtemperature; pouring cement, mineral pigment accounting for 3%-6% of the weight of the cement and stone particles into a terrazzo machine for mixing; and placing sealing partition plates on the periphery of a foamed ceramic partition plate, and flatly laying terrazzo materials on the surface of the foamed ceramic partition plate. The foamed ceramic terrazzo composite board is low in manufacturingcost and good in fireproof and waterproof performance.
本发明提供一种发泡陶瓷水磨石复合板及其制备方法，其中，制备方法如下：将40%铁尾矿粉料，40%珍珠岩尾矿，19.6%高岭土，以及0.4%发泡剂放入球磨机内；按照球：粉料：水为1.6：1.0：0.6的重量比加入水和高铝研磨球，再加入0.5%粉料总重的三聚磷酸钠球磨6h；将发泡陶瓷用混合料放入耐火模具内；将耐火模具放在隧道窑的窑车台面或辊道窑的辊棒上，经过1180°高温烧制0.5h后，快速降温至室温；往水磨石机内倒入水泥、3%～6%水泥重量的矿物颜料、以及石粒进行拌和；在发泡陶瓷隔墙板的四周放置密封隔板，将水磨石料平铺在发泡陶瓷隔墙板的表面。本发明的发泡陶瓷水磨石复合板造价低、防火、防水性能好。
Foamed ceramic terrazzo composite board and preparation method thereof
一种发泡陶瓷水磨石复合板及其制备方法
PENG WEISHUN (author)
2020-11-27
Patent
Electronic Resource
Chinese
Foamed ceramic composite additive, foamed ceramic and preparation method thereof
| European Patent Office | 2021
Foamed ceramic GRC composite board and preparation method thereof
| European Patent Office | 2024
Terrazzo. the timeless allure of terrazzo
British Library Online Contents | 2001