Roller kiln low-temperature sintered colorful halo crystal glaze and preparation method thereof
The invention relates to the technical field of new ceramic materials, and particularly discloses a roller kiln low-temperature sintered colorful halo crystal glaze which comprises a ground glaze anda cover glaze, and the ground glaze comprises the following components in parts by weight: 80 to 90 parts of lead-zinc frit and 10 to 20 parts of pigment; the cover glaze is prepared from the following components in parts by weight: 50 to 70 parts of high-boron frit, 5 to 10 parts of titanium dioxide, 10 to 20 parts of zinc oxide, 5 to 15 parts of talc, 0 to 10 parts of calcite and 17 to 30 partsof seeding colorant, wherein the seeding colorant is prepared from manganese dioxide, vanadium pentoxide and copper oxide. The preparation method of the roller kiln low-temperature sintered colorful halo crystal glaze comprises the steps of preparing the ground glaze and cover glaze, glazing and sintering, wherein the highest sintering temperature is 1125 to 1135 DEG C, and the sintering period is190 to 210 min. The crystal glaze suitable for roller kiln low-temperature sintering is prepared, the glaze surface can show a circle of colorful halo under the sun, and the process effect of metal and crystal glaze is achieved.
本发明涉及陶瓷新材料技术领域，具体公开了一种辊道窑低温烧成七彩光晕结晶釉，包括底釉和面釉，底釉的组成按重量份计为：铅锌熔块80‑90份，色料10‑20份；面釉的组成按重量份计为：高硼熔块50‑70份，二氧化钛5‑10份，氧化锌10‑20份，滑石5‑15份，方解石0‑10份，引晶着色剂17‑30份，引晶着色剂为二氧化锰、五氧化二矾和氧化铜。辊道窑低温烧成七彩光晕结晶釉的制备方法包括底釉和面釉的制备及施釉与烧成，其最高烧成温度为1125‑1135℃，烧成周期为190‑210min，制备了一种适于辊道窑低温烧成的结晶釉，釉面在太阳下可呈现一圈圈的七彩光晕，兼具金属与结晶釉的工艺效果。
Roller kiln low-temperature sintered colorful halo crystal glaze and preparation method thereof
The invention relates to the technical field of new ceramic materials, and particularly discloses a roller kiln low-temperature sintered colorful halo crystal glaze which comprises a ground glaze anda cover glaze, and the ground glaze comprises the following components in parts by weight: 80 to 90 parts of lead-zinc frit and 10 to 20 parts of pigment; the cover glaze is prepared from the following components in parts by weight: 50 to 70 parts of high-boron frit, 5 to 10 parts of titanium dioxide, 10 to 20 parts of zinc oxide, 5 to 15 parts of talc, 0 to 10 parts of calcite and 17 to 30 partsof seeding colorant, wherein the seeding colorant is prepared from manganese dioxide, vanadium pentoxide and copper oxide. The preparation method of the roller kiln low-temperature sintered colorful halo crystal glaze comprises the steps of preparing the ground glaze and cover glaze, glazing and sintering, wherein the highest sintering temperature is 1125 to 1135 DEG C, and the sintering period is190 to 210 min. The crystal glaze suitable for roller kiln low-temperature sintering is prepared, the glaze surface can show a circle of colorful halo under the sun, and the process effect of metal and crystal glaze is achieved.
本发明涉及陶瓷新材料技术领域，具体公开了一种辊道窑低温烧成七彩光晕结晶釉，包括底釉和面釉，底釉的组成按重量份计为：铅锌熔块80‑90份，色料10‑20份；面釉的组成按重量份计为：高硼熔块50‑70份，二氧化钛5‑10份，氧化锌10‑20份，滑石5‑15份，方解石0‑10份，引晶着色剂17‑30份，引晶着色剂为二氧化锰、五氧化二矾和氧化铜。辊道窑低温烧成七彩光晕结晶釉的制备方法包括底釉和面釉的制备及施釉与烧成，其最高烧成温度为1125‑1135℃，烧成周期为190‑210min，制备了一种适于辊道窑低温烧成的结晶釉，釉面在太阳下可呈现一圈圈的七彩光晕，兼具金属与结晶釉的工艺效果。
Roller kiln low-temperature sintered colorful halo crystal glaze and preparation method thereof
一种辊道窑低温烧成七彩光晕结晶釉及其制备方法
CHEN DIQING (author)
2021-01-26
Patent
Electronic Resource
Chinese
Colorful altered-glaze Jian cup and preparation process thereof
| European Patent Office | 2021
Sanitary ceramic glaze with colorful effect, preparation method thereof and sanitary ceramic
| European Patent Office | 2020