High-titanium blast furnace slag pervious concrete and using method thereof
The invention discloses high-titanium blast furnace slag pervious concrete and a using method thereof. The high-titanium blast furnace slag pervious concrete is prepared from, by mass, 1330-1360 partsof high-titanium blast furnace slag particles, 120-150 parts of high-titanium blast furnace water-quenched slag, 210-240 parts of cement, 9-11 parts of superplasticizer, 12-13 parts of enhancer, 13-15 parts of pigment and 90-95 parts of water. The preparation method comprises the following steps: uniformly mixing and stirring the raw materials, conducting paving and rolling on the ground, and naturally conducting curing for 12-15 days. According to the method, the utilization amount of waste resource blast furnace slag in the metallurgical process is effectively increased, and the productioncost is reduced.
本发明公开了一种高钛型高炉渣透水混凝土及其使用方法，按质量份数计，包括以下组分：高钛型高炉渣的颗粒1330～1360份、高钛高炉水淬渣120～150份、水泥210～240份、高效减水剂9～11份、增强剂12～13份、颜料13～15份和水90～95份；将各原料混合搅拌均匀，在地面摊铺、碾压，自然养护12‑15天后即可。本发明有效提高了冶金过程中废弃资源高炉渣利用量，降低了生产成本。
High-titanium blast furnace slag pervious concrete and using method thereof
The invention discloses high-titanium blast furnace slag pervious concrete and a using method thereof. The high-titanium blast furnace slag pervious concrete is prepared from, by mass, 1330-1360 partsof high-titanium blast furnace slag particles, 120-150 parts of high-titanium blast furnace water-quenched slag, 210-240 parts of cement, 9-11 parts of superplasticizer, 12-13 parts of enhancer, 13-15 parts of pigment and 90-95 parts of water. The preparation method comprises the following steps: uniformly mixing and stirring the raw materials, conducting paving and rolling on the ground, and naturally conducting curing for 12-15 days. According to the method, the utilization amount of waste resource blast furnace slag in the metallurgical process is effectively increased, and the productioncost is reduced.
本发明公开了一种高钛型高炉渣透水混凝土及其使用方法，按质量份数计，包括以下组分：高钛型高炉渣的颗粒1330～1360份、高钛高炉水淬渣120～150份、水泥210～240份、高效减水剂9～11份、增强剂12～13份、颜料13～15份和水90～95份；将各原料混合搅拌均匀，在地面摊铺、碾压，自然养护12‑15天后即可。本发明有效提高了冶金过程中废弃资源高炉渣利用量，降低了生产成本。
High-titanium blast furnace slag pervious concrete and using method thereof
一种高钛型高炉渣透水混凝土及其使用方法
YAO ZENGYUAN (author) / WANG BIN (author) / FENG GUANGLI (author) / YANG ZHIYUAN (author) / HAN GUOBING (author)
2021-02-23
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Concrete aggregate containing high-titanium blast furnace slag and preparation method thereof
| European Patent Office | 2022
| European Patent Office | 2015
| European Patent Office | 2015