Large-scale SQ type manganese zinc ferrite magnetic core and preparation method thereof
The invention discloses a large-scale SQ type manganese zinc ferrite magnetic core which comprises the following raw materials in percentage by weight: 68-70% of Fe2O3, 14-16% of Mn3O4, 14-16% of ZnO,PVA glue and an additive, wherein the weight percentage of the raw materials with the particle size of 60-160 meshes is 80-90%, and the particle sizes of the rest raw materials are greater than 160 meshes. Meanwhile, the invention also discloses a preparation method of the large-scale SQ type manganese zinc ferrite magnetic core. The method comprises the following steps: sintering the raw materials according to a certain temperature curve, and cooling under the condition that the oxygen partial pressure coefficient is 7.5-8, and molding. Under the support of an original dry process productionkey technology, the method is aimed at the production of high frequency, high impedance and low power consumption materials: adopting a good basic formula and additive combination, limiting the suitable sintering atmosphere curve and strict process control and management, and finally producing a new broadband high-impedance material.
本发明公开了一种大型SQ型锰锌铁氧体磁芯,包括以下重量百分比的原料:Fe2O3 68‑70%、Mn3O4 14‑16%、ZnO 14‑16%、PVA胶和添加剂;其中粒径为60‑160目的原料重量百分比为80‑90%,其余原料粒径大于160目。同时,本发明还公开了大型SQ型锰锌铁氧体磁芯的制备方法,包括一定的温度曲线对原料进行烧结后,最后在氧分压系数7.5‑8的条件下降温后成型。本发明在原有干法工艺生产关键技术的支持下,针对高频、高阻抗、低功耗材料进行生产,采用良好的基础配方和添加剂组合相搭配,且限定适合的烧结气氛曲线以及严格的工艺控制与管理,最终制得新的宽频高阻抗材料。
Large-scale SQ type manganese zinc ferrite magnetic core and preparation method thereof
The invention discloses a large-scale SQ type manganese zinc ferrite magnetic core which comprises the following raw materials in percentage by weight: 68-70% of Fe2O3, 14-16% of Mn3O4, 14-16% of ZnO,PVA glue and an additive, wherein the weight percentage of the raw materials with the particle size of 60-160 meshes is 80-90%, and the particle sizes of the rest raw materials are greater than 160 meshes. Meanwhile, the invention also discloses a preparation method of the large-scale SQ type manganese zinc ferrite magnetic core. The method comprises the following steps: sintering the raw materials according to a certain temperature curve, and cooling under the condition that the oxygen partial pressure coefficient is 7.5-8, and molding. Under the support of an original dry process productionkey technology, the method is aimed at the production of high frequency, high impedance and low power consumption materials: adopting a good basic formula and additive combination, limiting the suitable sintering atmosphere curve and strict process control and management, and finally producing a new broadband high-impedance material.
本发明公开了一种大型SQ型锰锌铁氧体磁芯,包括以下重量百分比的原料:Fe2O3 68‑70%、Mn3O4 14‑16%、ZnO 14‑16%、PVA胶和添加剂;其中粒径为60‑160目的原料重量百分比为80‑90%,其余原料粒径大于160目。同时,本发明还公开了大型SQ型锰锌铁氧体磁芯的制备方法,包括一定的温度曲线对原料进行烧结后,最后在氧分压系数7.5‑8的条件下降温后成型。本发明在原有干法工艺生产关键技术的支持下,针对高频、高阻抗、低功耗材料进行生产,采用良好的基础配方和添加剂组合相搭配,且限定适合的烧结气氛曲线以及严格的工艺控制与管理,最终制得新的宽频高阻抗材料。
Large-scale SQ type manganese zinc ferrite magnetic core and preparation method thereof
一种大型SQ型锰锌铁氧体磁芯及制备方法
CHEN HUABIN (author) / XIN BENKUI (author) / KONG ZHIQIANG (author) / YI YUXIANG (author) / WANG WENBIN (author)
2021-03-12
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
/
B28B
Formgeben von Ton oder anderen keramischen Stoffzusammensetzungen, Schlacke oder von Mischungen, die zementartiges Material enthalten, z.B. Putzmörtel
,
SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS, SLAG OR MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
/
H01F
MAGNETS
,
Magnete
Manganese zinc ferrite magnetic core and preparation method thereof
European Patent Office | 2021
|Manufacturing method of manganese-zinc ferrite large magnetic core
European Patent Office | 2021
|Preparation method of manganese zinc ferrite large-size magnetic ring
European Patent Office | 2024
|Manganese zinc ferrite magnetic dielectric powder and preparation method thereof
European Patent Office | 2024
|