The invention discloses a building indoor decoration method. The building indoor decoration method comprises the following steps that (1) self-leveling mortar and water are stirred and mixed accordingto a weight ratio of 5: 1, and the mixture is coated on the indoor ground through a leveling machine to form a bottom layer; the self-leveling mortar is prepared from the following substances in parts by weight: 20-25 parts of 52.5 R silicate cement, 5-10 parts of high-alumina cement, 1-2 parts of a flow increasing agent, 15-25 parts of calcium carbonate with the particle size of 50-100 microns,30-50 parts of silica sand with the particle size of 0.1-0.5 mm, 0.5-1 part of an early strength agent, 0.5-1 part of a retarder, 1-3 parts of quick lime, 2-4 parts of redispersible latex powder, 0.5-1 part of a water-retaining agent and 0.5-1 part of a defoamer; (2) the bottom layer is coated with a modeling layer; and (3) solvent-free epoxy resin and a curing agent are mixed according to the weight ratio of 2: 1, and the mixture is trowelled on the modeling layer to form a wear-resistant transparent surface layer. According to the building indoor decoration method, primary leveling is carried out before final leveling of the mortar, so that the efficiency is improved, the compactness is improved, the surface of the leveled mortar is smooth, and bubbles are avoided.
本发明公开了一种建筑室内装修方法，包括以下步骤：(1)将自找平砂浆与水按5∶1的重量比搅拌、混合，通过找平机涂布于室内地面形成底层；所述自找平砂浆由下列物质按份额调制而成：52.5R的硅酸盐水泥20‑25份、高铝水泥5‑10份、增流剂1‑2份、粒径为50‑100微米的碳酸钙15‑25份、粒径为0.1‑0.5毫米的硅砂30‑50份、早强剂0.5‑1份、缓凝剂0.5‑1份、生石灰1‑3份、再分散乳胶粉2‑4份、保水剂0.5‑1份、消泡剂0.5‑1份；(2)在底层上涂铺造型层；(3)将无溶剂环氧树脂和固化剂按2∶1的重量比混合，镘布在造型层上，形成耐磨透明面层即可；本发明通过在对砂浆最终找平前进行初步找平，从而提高效率，提高密实性，使得找平之后的砂浆表面平整，避免出现气泡。
The invention discloses a building indoor decoration method. The building indoor decoration method comprises the following steps that (1) self-leveling mortar and water are stirred and mixed accordingto a weight ratio of 5: 1, and the mixture is coated on the indoor ground through a leveling machine to form a bottom layer; the self-leveling mortar is prepared from the following substances in parts by weight: 20-25 parts of 52.5 R silicate cement, 5-10 parts of high-alumina cement, 1-2 parts of a flow increasing agent, 15-25 parts of calcium carbonate with the particle size of 50-100 microns,30-50 parts of silica sand with the particle size of 0.1-0.5 mm, 0.5-1 part of an early strength agent, 0.5-1 part of a retarder, 1-3 parts of quick lime, 2-4 parts of redispersible latex powder, 0.5-1 part of a water-retaining agent and 0.5-1 part of a defoamer; (2) the bottom layer is coated with a modeling layer; and (3) solvent-free epoxy resin and a curing agent are mixed according to the weight ratio of 2: 1, and the mixture is trowelled on the modeling layer to form a wear-resistant transparent surface layer. According to the building indoor decoration method, primary leveling is carried out before final leveling of the mortar, so that the efficiency is improved, the compactness is improved, the surface of the leveled mortar is smooth, and bubbles are avoided.
本发明公开了一种建筑室内装修方法，包括以下步骤：(1)将自找平砂浆与水按5∶1的重量比搅拌、混合，通过找平机涂布于室内地面形成底层；所述自找平砂浆由下列物质按份额调制而成：52.5R的硅酸盐水泥20‑25份、高铝水泥5‑10份、增流剂1‑2份、粒径为50‑100微米的碳酸钙15‑25份、粒径为0.1‑0.5毫米的硅砂30‑50份、早强剂0.5‑1份、缓凝剂0.5‑1份、生石灰1‑3份、再分散乳胶粉2‑4份、保水剂0.5‑1份、消泡剂0.5‑1份；(2)在底层上涂铺造型层；(3)将无溶剂环氧树脂和固化剂按2∶1的重量比混合，镘布在造型层上，形成耐磨透明面层即可；本发明通过在对砂浆最终找平前进行初步找平，从而提高效率，提高密实性，使得找平之后的砂浆表面平整，避免出现气泡。
Building indoor decoration method
一种建筑室内装修方法
ZHOU YEWEI (author)
2021-03-19
Patent
Electronic Resource
Chinese
IPC:
E04F
FINISHING WORK ON BUILDINGS, e.g. STAIRS, FLOORS
,
Ausbau von Bauwerken, z.B. Treppen, Fußböden