Mud glaze formula for high-temperature firing of bone daily-use porcelain
The invention relates to a mud glaze formula for high-temperature firing of bone daily porcelain, and belongs to the technical field of ceramic products. The pug and the glaze are prepared from the following formula components in parts by weight: pug: 70-80 parts of talc, 3-4 parts of bone charcoal powder, 3-6 parts of feldspar, 4-7 parts of bentonite, 91-3 parts of Datong soil and 0.2-0.5 part ofsodium humate; glaze: 55-62 parts of potassium feldspar, 9-12 parts of quartz, 9-11 parts of Longyan clay, 3-4 parts of lepidolite, 3-5 parts of zinc oxide, 9-10 parts of waste porcelain powder and 2-3 parts of bone black powder. With performance of pug and glaze preparation, molding, drying, glazing and high-temperature firing, the product is obtained, the firing time is 8-12 hours, and the highest firing temperature is 1280-1320 DEG C. The novel bone daily-use porcelain fired by the method is good in transparency, strength and whiteness, smooth and clean, and high in ornamental value, so that the novel bone daily-use porcelain has a wide application prospect.
本发明涉及一种用于高温烧成骨质日用瓷的泥釉料配方，属于陶瓷制品技术领域。其泥料和釉料配方成分的重量份数为，泥料：滑石70‑80份、骨炭粉3‑4份、长石3‑6份、膨润土4‑7份、大同土9‑13份、腐殖酸钠0.2‑0.5份；釉料：钾长石55‑62份、石英9‑12份、龙岩土9‑11份、锂云母3‑4份、氧化锌3‑5份、废瓷粉9‑10份、骨炭粉2‑3份经过泥料和釉料制备、成型、干燥、施釉、高温烧成获得制品，其烧成时间为8‑12h，最高烧成温度为1280‑1320℃。本发明烧成的新型骨质日用瓷透明度、强度和白度好，光洁、观赏价值高，因此具有广阔的应用前景。
Mud glaze formula for high-temperature firing of bone daily-use porcelain
The invention relates to a mud glaze formula for high-temperature firing of bone daily porcelain, and belongs to the technical field of ceramic products. The pug and the glaze are prepared from the following formula components in parts by weight: pug: 70-80 parts of talc, 3-4 parts of bone charcoal powder, 3-6 parts of feldspar, 4-7 parts of bentonite, 91-3 parts of Datong soil and 0.2-0.5 part ofsodium humate; glaze: 55-62 parts of potassium feldspar, 9-12 parts of quartz, 9-11 parts of Longyan clay, 3-4 parts of lepidolite, 3-5 parts of zinc oxide, 9-10 parts of waste porcelain powder and 2-3 parts of bone black powder. With performance of pug and glaze preparation, molding, drying, glazing and high-temperature firing, the product is obtained, the firing time is 8-12 hours, and the highest firing temperature is 1280-1320 DEG C. The novel bone daily-use porcelain fired by the method is good in transparency, strength and whiteness, smooth and clean, and high in ornamental value, so that the novel bone daily-use porcelain has a wide application prospect.
本发明涉及一种用于高温烧成骨质日用瓷的泥釉料配方，属于陶瓷制品技术领域。其泥料和釉料配方成分的重量份数为，泥料：滑石70‑80份、骨炭粉3‑4份、长石3‑6份、膨润土4‑7份、大同土9‑13份、腐殖酸钠0.2‑0.5份；釉料：钾长石55‑62份、石英9‑12份、龙岩土9‑11份、锂云母3‑4份、氧化锌3‑5份、废瓷粉9‑10份、骨炭粉2‑3份经过泥料和釉料制备、成型、干燥、施釉、高温烧成获得制品，其烧成时间为8‑12h，最高烧成温度为1280‑1320℃。本发明烧成的新型骨质日用瓷透明度、强度和白度好，光洁、观赏价值高，因此具有广阔的应用前景。
Mud glaze formula for high-temperature firing of bone daily-use porcelain
一种用于高温烧成骨质日用瓷的泥釉料配方
LI DONGGEN (author) / PENG YUNGEN (author) / ZHAO LIMING (author) / LI CHAO (author) / PENG SHUIGEN (author) / YANG FENG (author)
2021-03-26
Patent
Electronic Resource
Chinese