High-wear-resistance marble-imitated ceramic tile and preparation method thereof
The invention discloses a high-wear-resistance marble-imitated ceramic tile and a preparation method thereof. The preparation method of the high-wear-resistance marble-imitated ceramic tile comprisesthe steps of A, obtaining ground coat; B, obtaining wear-resistant glaze, wherein the wear-resistant glaze is prepared from the following raw materials in parts by weight: 10-12 parts of potassium feldspar, 18-20 parts of albite, 2-3 parts of limestone, 12-14 parts of calcined talcum powder, 19-20 parts of barium carbonate, 5-7 parts of calcined zinc oxide, 8-9 parts of corundum powder, 18-20 parts of frit and 9-11 parts of kaolin; C, obtaining wear-resistant particle glaze; D, applying the ground coat to a green tile; E, spraying the wear-resistant glaze on the ground coat layer; F, sprayingthe wear-resistant particle glaze on the wear-resistant glaze layer; and G, drying and firing the green tile. According to the preparation method of the high-wear-resistance marble-imitated ceramic tile provided by the technical scheme, the glazing thickness is small, but the wear resistance is high. The invention further provides a high-wear-resistance marble-imitated ceramic tile prepared through the preparation method of the high-wear-resistance marble-imitated ceramic tile, which is high in hardness and good in wear resistance.
本发明公开了高耐磨仿大理石瓷砖及其制备方法,高耐磨仿大理石瓷砖的制备方法包括以下步骤:A、获得底釉;B、获得耐磨釉;其中,耐磨釉包括以下原料:钾长石10~12份、钠长石18~20份、石灰石2~3份、煅烧滑石粉12~14份、碳酸钡19~20份、煅烧氧化锌5~7份、刚玉粉8~9份、熔块18~20份和高岭土9~11份;C、获得耐磨粒子釉;D、将底釉布施在砖坯上;E、将耐磨釉喷涂在底釉层上;F、将耐磨粒子釉喷涂在耐磨釉层上;G、将砖坯进行烘干和烧制。本技术方案提出的一种高耐磨仿大理石瓷砖的制备方法,其施釉厚度薄,但耐磨能力强。进而提出的一种上述高耐磨仿大理石瓷砖的制备方法制备的高耐磨仿大理石瓷砖,其硬度高且耐磨性能好。
High-wear-resistance marble-imitated ceramic tile and preparation method thereof
The invention discloses a high-wear-resistance marble-imitated ceramic tile and a preparation method thereof. The preparation method of the high-wear-resistance marble-imitated ceramic tile comprisesthe steps of A, obtaining ground coat; B, obtaining wear-resistant glaze, wherein the wear-resistant glaze is prepared from the following raw materials in parts by weight: 10-12 parts of potassium feldspar, 18-20 parts of albite, 2-3 parts of limestone, 12-14 parts of calcined talcum powder, 19-20 parts of barium carbonate, 5-7 parts of calcined zinc oxide, 8-9 parts of corundum powder, 18-20 parts of frit and 9-11 parts of kaolin; C, obtaining wear-resistant particle glaze; D, applying the ground coat to a green tile; E, spraying the wear-resistant glaze on the ground coat layer; F, sprayingthe wear-resistant particle glaze on the wear-resistant glaze layer; and G, drying and firing the green tile. According to the preparation method of the high-wear-resistance marble-imitated ceramic tile provided by the technical scheme, the glazing thickness is small, but the wear resistance is high. The invention further provides a high-wear-resistance marble-imitated ceramic tile prepared through the preparation method of the high-wear-resistance marble-imitated ceramic tile, which is high in hardness and good in wear resistance.
本发明公开了高耐磨仿大理石瓷砖及其制备方法,高耐磨仿大理石瓷砖的制备方法包括以下步骤:A、获得底釉;B、获得耐磨釉;其中,耐磨釉包括以下原料:钾长石10~12份、钠长石18~20份、石灰石2~3份、煅烧滑石粉12~14份、碳酸钡19~20份、煅烧氧化锌5~7份、刚玉粉8~9份、熔块18~20份和高岭土9~11份;C、获得耐磨粒子釉;D、将底釉布施在砖坯上;E、将耐磨釉喷涂在底釉层上;F、将耐磨粒子釉喷涂在耐磨釉层上;G、将砖坯进行烘干和烧制。本技术方案提出的一种高耐磨仿大理石瓷砖的制备方法,其施釉厚度薄,但耐磨能力强。进而提出的一种上述高耐磨仿大理石瓷砖的制备方法制备的高耐磨仿大理石瓷砖,其硬度高且耐磨性能好。
High-wear-resistance marble-imitated ceramic tile and preparation method thereof
高耐磨仿大理石瓷砖及其制备方法
XIE YUERONG (author) / HUO ZHENHUI (author) / XU PENGFEI (author)
2021-04-02
Patent
Electronic Resource
Chinese
Marble-imitated ceramic tile and preparation method thereof
European Patent Office | 2022
|Natural-marble-imitated ceramic tile and preparation method thereof
European Patent Office | 2021
|European Patent Office | 2023
|European Patent Office | 2023
|Phosphogypsum base material marble-imitated floor tile and preparation method thereof
European Patent Office | 2015
|