The invention discloses a ceramic processing technology which comprises the following steps: 1, modifying bentonite: adding bentonite into a surfactant, stirring at a low speed of 50-100r/min for 10-20min, washing with water, drying, and grinding to 50-100 meshes; in ceramic processing, spodumene is used as a base material, bentonite is treated in a surface agent, then blasting treatment is carried out, wollastonite in the surface agent is inserted into the bentonite in a penetrating mode, meanwhile, the effect of wollastonite on bentonite can be improved through shell powder, and therefore in the hot-pressing calcination process, the spodumene is jointly improved through bentonite and wollastonite.
本发明公开了一种陶瓷加工工艺,包括以下步骤：步骤一，膨润土的改性：将膨润土加入到表面剂中进行低速搅拌，搅拌转速为50‑100r/min，搅拌时间为10‑20min，然水洗、干燥，然后研磨至50‑100目。本发明陶瓷加工中以锂辉石为基料，通过膨润土在表面剂中处理，然后在通过爆破处理，从而将表面剂中的硅灰石穿插到膨润土中，同时通过贝壳粉能够提高硅灰石对膨润土的作用效果，进而在热压煅烧中，通过膨润土与硅灰石的对锂辉石共同改进。
The invention discloses a ceramic processing technology which comprises the following steps: 1, modifying bentonite: adding bentonite into a surfactant, stirring at a low speed of 50-100r/min for 10-20min, washing with water, drying, and grinding to 50-100 meshes; in ceramic processing, spodumene is used as a base material, bentonite is treated in a surface agent, then blasting treatment is carried out, wollastonite in the surface agent is inserted into the bentonite in a penetrating mode, meanwhile, the effect of wollastonite on bentonite can be improved through shell powder, and therefore in the hot-pressing calcination process, the spodumene is jointly improved through bentonite and wollastonite.
本发明公开了一种陶瓷加工工艺,包括以下步骤：步骤一，膨润土的改性：将膨润土加入到表面剂中进行低速搅拌，搅拌转速为50‑100r/min，搅拌时间为10‑20min，然水洗、干燥，然后研磨至50‑100目。本发明陶瓷加工中以锂辉石为基料，通过膨润土在表面剂中处理，然后在通过爆破处理，从而将表面剂中的硅灰石穿插到膨润土中，同时通过贝壳粉能够提高硅灰石对膨润土的作用效果，进而在热压煅烧中，通过膨润土与硅灰石的对锂辉石共同改进。
Ceramic processing technology
一种陶瓷加工工艺
GUO HUIHUI (author)
2021-04-13
Patent
Electronic Resource
Chinese