The invention relates to a firewood porcelain pea green glaze which is prepared from the following components by weight: 21.26 parts of quartz, 30.01 parts of feldspar, 12.35 parts of calcite, 20.85 parts of plant ash, 3.01 parts of spot fossil, 3.58 parts of phosphorus bone powder, 3.60 parts of agate stone, 2.25 parts of water bone stone, and 3.00 parts of white metal soil, the quartz is quartz sand, the content of quartz in the quartz sand is greater than or equal to 90%, the feldspar is one or a combination of albite and potassium feldspar, the phosphorus bone meal is any one of cattle bone meal, pig bone meal or horse bone meal, and the content of phosphorus is greater than or equal to 14.5%; the preparation method comprises the following steps: step 1, preparing a green body: preparing the green body for later use; step 2, grinding: weighing the components of the glaze according to the formula, and adding the materials into a Raymond mill for grinding; step 3, biscuit firing: obtaining a biscuit firing blank for use; step 4, glazing: glazing the biscuit firing blank; step 5, firing: firing the glazed biscuit firing blank; the glaze has the advantages that the preparation process is reasonable, the glossiness is good, and the glaze is stable and free of color blocks.
本发明涉及柴瓷豆绿釉，它是由各组分按照以下重量配比制成：石英21.26份、长石30.01份、方解石12.35份、草木灰20.85份、斑化石3.01份、磷骨粉3.58份、玛瑙石3.60份、水骨石2.25份、乌金土3.00份，石英采用的是石英砂，石英砂中石英的含量≥90%，长石为钠长石和钾长石中的一种或两种的组合，磷骨粉为牛骨粉、猪骨粉或马骨粉中任意一种，其中磷的含量≥14.5%；它的制成包括以下步骤：步骤1、坯体制备：制备坯体备用；步骤2、磨粉，按配方称取釉料的各组分，通将物料加入到雷蒙磨粉机中进行磨粉；步骤3、素烧，得到素烧坯，备用；步骤4、施釉，对素烧坯进行施釉；步骤5、烧成，对施釉后的素烧坯进行烧成；本发明具有制作过程合理、光泽度好、釉料稳定无色块的优点。
The invention relates to a firewood porcelain pea green glaze which is prepared from the following components by weight: 21.26 parts of quartz, 30.01 parts of feldspar, 12.35 parts of calcite, 20.85 parts of plant ash, 3.01 parts of spot fossil, 3.58 parts of phosphorus bone powder, 3.60 parts of agate stone, 2.25 parts of water bone stone, and 3.00 parts of white metal soil, the quartz is quartz sand, the content of quartz in the quartz sand is greater than or equal to 90%, the feldspar is one or a combination of albite and potassium feldspar, the phosphorus bone meal is any one of cattle bone meal, pig bone meal or horse bone meal, and the content of phosphorus is greater than or equal to 14.5%; the preparation method comprises the following steps: step 1, preparing a green body: preparing the green body for later use; step 2, grinding: weighing the components of the glaze according to the formula, and adding the materials into a Raymond mill for grinding; step 3, biscuit firing: obtaining a biscuit firing blank for use; step 4, glazing: glazing the biscuit firing blank; step 5, firing: firing the glazed biscuit firing blank; the glaze has the advantages that the preparation process is reasonable, the glossiness is good, and the glaze is stable and free of color blocks.
本发明涉及柴瓷豆绿釉，它是由各组分按照以下重量配比制成：石英21.26份、长石30.01份、方解石12.35份、草木灰20.85份、斑化石3.01份、磷骨粉3.58份、玛瑙石3.60份、水骨石2.25份、乌金土3.00份，石英采用的是石英砂，石英砂中石英的含量≥90%，长石为钠长石和钾长石中的一种或两种的组合，磷骨粉为牛骨粉、猪骨粉或马骨粉中任意一种，其中磷的含量≥14.5%；它的制成包括以下步骤：步骤1、坯体制备：制备坯体备用；步骤2、磨粉，按配方称取釉料的各组分，通将物料加入到雷蒙磨粉机中进行磨粉；步骤3、素烧，得到素烧坯，备用；步骤4、施釉，对素烧坯进行施釉；步骤5、烧成，对施釉后的素烧坯进行烧成；本发明具有制作过程合理、光泽度好、釉料稳定无色块的优点。
Firewood porcelain pea green glaze
柴瓷豆绿釉