Inorganic environment-friendly ceramic cement, application, processing technology and processing equipment
The invention belongs to the technical field of adhesives, relates to inorganic environment-friendly ceramic cement, application, a processing technology and processing equipment, which solve the problems of poor environmental protection property and the like of cement. The ceramic cement comprises 12% to 28% of magnesium oxide, 22% to 38% of potassium monophosphate and 22% to 38% of granite sand or granite, as well as 18% to 36% of calcium silicate, 22% to 34% of metakaolin or 18% to 42% of fly ash. During application, the ceramic cement can be stirred with water, and then irrigation, smearing or spraying are carried out. The processing technology of the ceramic cement comprises four steps of feeding, weighing, mixing and filling. Correspondingly, the processing equipment comprises a feeding hopper, a weighing device, a stirring barrel and a filling machine. Compared with the prior art, the advantages of good environmental protection property and better waterproofness, water resistance and corrosion resistance are achieved.
本发明属于粘合剂技术领域，涉及一种无机环保陶瓷水泥、应用、加工工艺及加工设备，其解决了水泥的环保性差等问题。陶瓷水泥包括12％至28％的氧化镁、22％至38％的单磷酸钾和22％至38％的花岗石砂或花岗岩，以及18％至36％硅酸钙、22％至34％偏高岭土或18％至42％粉煤灰。在应用时，可将上述陶瓷水泥与水进行搅拌，然后进行浇灌、涂抹或喷涂。而本陶瓷水泥的加工工艺包括：进料、称重、混料及灌装4个步骤。对应的，其加工设备包括进料斗、称重器、搅拌筒及灌装机。与现有技术相比，本发明具有良好的环保性，且防水性、防水性、防腐性均较好。
Inorganic environment-friendly ceramic cement, application, processing technology and processing equipment
The invention belongs to the technical field of adhesives, relates to inorganic environment-friendly ceramic cement, application, a processing technology and processing equipment, which solve the problems of poor environmental protection property and the like of cement. The ceramic cement comprises 12% to 28% of magnesium oxide, 22% to 38% of potassium monophosphate and 22% to 38% of granite sand or granite, as well as 18% to 36% of calcium silicate, 22% to 34% of metakaolin or 18% to 42% of fly ash. During application, the ceramic cement can be stirred with water, and then irrigation, smearing or spraying are carried out. The processing technology of the ceramic cement comprises four steps of feeding, weighing, mixing and filling. Correspondingly, the processing equipment comprises a feeding hopper, a weighing device, a stirring barrel and a filling machine. Compared with the prior art, the advantages of good environmental protection property and better waterproofness, water resistance and corrosion resistance are achieved.
本发明属于粘合剂技术领域，涉及一种无机环保陶瓷水泥、应用、加工工艺及加工设备，其解决了水泥的环保性差等问题。陶瓷水泥包括12％至28％的氧化镁、22％至38％的单磷酸钾和22％至38％的花岗石砂或花岗岩，以及18％至36％硅酸钙、22％至34％偏高岭土或18％至42％粉煤灰。在应用时，可将上述陶瓷水泥与水进行搅拌，然后进行浇灌、涂抹或喷涂。而本陶瓷水泥的加工工艺包括：进料、称重、混料及灌装4个步骤。对应的，其加工设备包括进料斗、称重器、搅拌筒及灌装机。与现有技术相比，本发明具有良好的环保性，且防水性、防水性、防腐性均较好。
Inorganic environment-friendly ceramic cement, application, processing technology and processing equipment
一种无机环保陶瓷水泥、应用、加工工艺及加工设备
FANG XIANQIN (author)
2021-09-21
Patent
Electronic Resource
Chinese
Environment-friendly processing equipment for thermal insulation ceramic tiles
| European Patent Office | 2022
Environment-friendly antibacterial ceramic blank and processing technology thereof
| European Patent Office | 2021
Environment-friendly inorganic ceramic pigment as well as preparation method and application thereof
| European Patent Office | 2024
Environment-friendly cement mixed material, cement and application thereof
| European Patent Office | 2016