Microporous light-weight washing water pumice stone and preparation method thereof
The invention relates to microporous light-weight washing water pumice and a preparation method thereof.The microporous light-weight washing water pumice is prepared from potassium-sodium feldspar, magnesian clay, wollastonite powder, aluminum oxide, burnout organic matter, a foaming agent, silicon carbide powder, limestone powder, carbon clay, boric acid and calcium oxide. The preparation method of the microporous light-weight washing water pumice comprises the following steps of 1, preparing silicon carbide powder; 2, preparing a foaming agent; 3, preparing wollastonite powder; 4, preparing a first mixture; 5, preparing a second mixture; 6, forming in a forming stamping die; and 7, preparing the microporous light-weight washing water pumice with the weight of 5-15 g and the micropore diameter of 0.01-0.03 mm. The ratio of the use amount of the microporous light-weight washing water pumice to the natural volcanic pumice is 1:9, so that the use amount is greatly reduced, the production cost is saved, jean textile garments and cloth are not easily contaminated, ditches are not blocked by sand and stones, and substances harmful to a human body are not contained.
本发明涉及一种微孔轻质洗水浮石及其制备方法，所述微孔轻质洗水浮石由钾钠长石、镁质粘土、硅灰石粉、氧化铝、燃尽有机物、发泡剂、碳化硅粉、石灰石粉、碳黏土、硼酸、氧化钙组成，所述微孔轻质洗水浮石的制备方法如下：步骤1、制备碳化硅粉，步骤2、制备发泡剂，步骤3、制备硅灰石粉，步骤4、制备第一混合料，步骤5、制备第二混合料，步骤6、成型冲压模具内成型，步骤7、制备所述微孔轻质洗水浮石，所述微孔轻质洗水浮石的重量为5～15g、微孔直径为0.01～0.03mm，所述微孔轻质洗水浮石与天然火山浮石的用量之比为1:9，用量大大减少，节省生产成本，不易沾染牛仔纺织服装及布料，未出现沙石堵塞水沟，且不含对人体有害的物质。
Microporous light-weight washing water pumice stone and preparation method thereof
The invention relates to microporous light-weight washing water pumice and a preparation method thereof.The microporous light-weight washing water pumice is prepared from potassium-sodium feldspar, magnesian clay, wollastonite powder, aluminum oxide, burnout organic matter, a foaming agent, silicon carbide powder, limestone powder, carbon clay, boric acid and calcium oxide. The preparation method of the microporous light-weight washing water pumice comprises the following steps of 1, preparing silicon carbide powder; 2, preparing a foaming agent; 3, preparing wollastonite powder; 4, preparing a first mixture; 5, preparing a second mixture; 6, forming in a forming stamping die; and 7, preparing the microporous light-weight washing water pumice with the weight of 5-15 g and the micropore diameter of 0.01-0.03 mm. The ratio of the use amount of the microporous light-weight washing water pumice to the natural volcanic pumice is 1:9, so that the use amount is greatly reduced, the production cost is saved, jean textile garments and cloth are not easily contaminated, ditches are not blocked by sand and stones, and substances harmful to a human body are not contained.
本发明涉及一种微孔轻质洗水浮石及其制备方法，所述微孔轻质洗水浮石由钾钠长石、镁质粘土、硅灰石粉、氧化铝、燃尽有机物、发泡剂、碳化硅粉、石灰石粉、碳黏土、硼酸、氧化钙组成，所述微孔轻质洗水浮石的制备方法如下：步骤1、制备碳化硅粉，步骤2、制备发泡剂，步骤3、制备硅灰石粉，步骤4、制备第一混合料，步骤5、制备第二混合料，步骤6、成型冲压模具内成型，步骤7、制备所述微孔轻质洗水浮石，所述微孔轻质洗水浮石的重量为5～15g、微孔直径为0.01～0.03mm，所述微孔轻质洗水浮石与天然火山浮石的用量之比为1:9，用量大大减少，节省生产成本，不易沾染牛仔纺织服装及布料，未出现沙石堵塞水沟，且不含对人体有害的物质。
Microporous light-weight washing water pumice stone and preparation method thereof
一种微孔轻质洗水浮石及其制备方法
LIN BINGNAN (author)
2021-09-28
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Artificial ceramic washing water pumice stone and preparation method thereof
| European Patent Office | 2021
Artificial plastic pumice stone and preparation method thereof
| European Patent Office | 2022
| ASCE | 2021
| Engineering Index Backfile | 1950