High-stability in-glaze decoration porcelain for daily use
The invention relates to the technical field of porcelain, and discloses a high-stability in-glaze decoration porcelain for daily use. A manufacturing method of the high-stability in-glaze decoration porcelain for daily use comprises the following steps of: 1, proportioning the following raw materials: 8% of fluorite, 12% of sepiolite, 4% of barite, 1% of magnesium borate whiskers, 10% of sodium alginate and 65% of clay; 2, selecting ingredients: selecting a mixture formed by combining vermiculite, montmorillonite and kaolin according to a mass ratio of 0.87: 1: 5; and 3, crushing the raw materials: putting the selected high-quality barite, fluorite and sepiolite into crushing equipment for crushing, screening the barite, fluorite and sepiolite by using a 200-mesh sieve after crushing is completed, performing magnetic separation on the screened powder, and mixing the powder with clay after magnetic separation is completed, and putting the mixture obtained after mixing into grinding equipment for fine grinding. According to the high-stability in-glaze decoration porcelain for daily use, the stability of the in-glaze decoration porcelain for daily use is improved, and the yield of the in-glaze decoration porcelain for daily use is effectively improved.
本发明涉及瓷器技术领域，且公开了高稳定性釉中彩日用瓷，所述高稳定性釉中彩日用瓷的制作方法包括以下步骤：步骤一、原料配比：萤石8%、海泡石12%、重晶石4%、硼酸镁晶须1%、海藻酸钠10%、粘土65%；步骤二、选取配料：选取质量比为0.87:1:5的蛭石、蒙脱土和高岭土组合而成的混合料；步骤三、原料粉碎：将选取的优质重晶石、萤石和海泡石放入粉碎设备中进行粉碎，粉碎完成后使用200目筛对重晶石、萤石和海泡石进行筛选，对筛分得到的粉末进行磁选，磁选完成后将粉末与粘土混合，混合后得到的混合物放入研磨设备中进行精磨。该高稳定性釉中彩日用瓷提高了釉中彩日用瓷的稳定性，有效的提高了釉中彩日用瓷的成品率。
High-stability in-glaze decoration porcelain for daily use
The invention relates to the technical field of porcelain, and discloses a high-stability in-glaze decoration porcelain for daily use. A manufacturing method of the high-stability in-glaze decoration porcelain for daily use comprises the following steps of: 1, proportioning the following raw materials: 8% of fluorite, 12% of sepiolite, 4% of barite, 1% of magnesium borate whiskers, 10% of sodium alginate and 65% of clay; 2, selecting ingredients: selecting a mixture formed by combining vermiculite, montmorillonite and kaolin according to a mass ratio of 0.87: 1: 5; and 3, crushing the raw materials: putting the selected high-quality barite, fluorite and sepiolite into crushing equipment for crushing, screening the barite, fluorite and sepiolite by using a 200-mesh sieve after crushing is completed, performing magnetic separation on the screened powder, and mixing the powder with clay after magnetic separation is completed, and putting the mixture obtained after mixing into grinding equipment for fine grinding. According to the high-stability in-glaze decoration porcelain for daily use, the stability of the in-glaze decoration porcelain for daily use is improved, and the yield of the in-glaze decoration porcelain for daily use is effectively improved.
本发明涉及瓷器技术领域，且公开了高稳定性釉中彩日用瓷，所述高稳定性釉中彩日用瓷的制作方法包括以下步骤：步骤一、原料配比：萤石8%、海泡石12%、重晶石4%、硼酸镁晶须1%、海藻酸钠10%、粘土65%；步骤二、选取配料：选取质量比为0.87:1:5的蛭石、蒙脱土和高岭土组合而成的混合料；步骤三、原料粉碎：将选取的优质重晶石、萤石和海泡石放入粉碎设备中进行粉碎，粉碎完成后使用200目筛对重晶石、萤石和海泡石进行筛选，对筛分得到的粉末进行磁选，磁选完成后将粉末与粘土混合，混合后得到的混合物放入研磨设备中进行精磨。该高稳定性釉中彩日用瓷提高了釉中彩日用瓷的稳定性，有效的提高了釉中彩日用瓷的成品率。
High-stability in-glaze decoration porcelain for daily use
高稳定性釉中彩日用瓷
XU CHUNJUN (author) / PENG YOUCAI (author) / GE GENGSHENG (author) / LIU JIN (author) / JIA YOUBAO (author)
2021-11-23
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Preparation method of wear-resistant glaze daily porcelain glaze
| European Patent Office | 2020
Preparation method of jade glaze daily porcelain with high thermal stability and high strength
| European Patent Office | 2020