The invention provides an inorganic water-based permeable crystallization waterproof material. The waterproof material is prepared from the following raw materials in parts by weight: 25 to 35 parts of silicate, 8 to 12 parts of carbonate, 1 to 3 parts of caustic soda, 0.5 to 1.5 parts of activated aluminum oxide, 8 to 12 parts of waterborne siloxane, 1 to 3 parts of tartaric acid, 1 to 3 parts of sodium gluconate, 1 to 3 parts of activated silicon dioxide, 1 to 3 parts of volcanic ash, 0.5 to 1.5 parts of bentonite, 0.1 to 0.3 part of a catalyst, 0.1 to 0.3 part of an additive and 32.7 to 42.7 parts of distilled water. The prepared novel environment-friendly permeable crystallization waterproof material is colorless, odorless, non-toxic and harmless like water in appearance, is simple and convenient to construct, only needs to be sprayed on the surface of concrete, then rapidly permeates into the concrete and chemically reacts with calcium ions in cement to generate crystals, the cement and sand are bonded together, and all micropores and capillary channels are blocked to form a waterproof layer with glass density, so that permanent water prevention is realized.
本发明提供了无机水性渗透结晶型防水材料，所述防水材料包括以下重量份原料：硅酸盐25‑35份、碳酸盐8‑12份、火碱1‑3份、活性氧化铝0.5‑1.5份、水性硅氧烷8‑12份、酒石酸1‑3份、葡萄糖酸钠1‑3份、活性二氧化硅1‑3份、火山灰1‑3份、膨润土0.5‑1.5份、催化剂0.1‑0.3份、助剂0.1‑0.3份、蒸馏水32.7‑42.7份。本发明制得的新型环保渗透结晶防水材料，外观像水一样无色无味，无毒无害，而且施工简单方便，只需喷在混凝土表面即可，然后该材料迅速渗透到混凝土内部，与水泥里面的钙离子发生化学反应产生结晶体，把水泥和沙子粘连在一起，堵塞住所有微孔和毛细通道，达到玻璃密度般的防水层，从而实现永久性防水。
The invention provides an inorganic water-based permeable crystallization waterproof material. The waterproof material is prepared from the following raw materials in parts by weight: 25 to 35 parts of silicate, 8 to 12 parts of carbonate, 1 to 3 parts of caustic soda, 0.5 to 1.5 parts of activated aluminum oxide, 8 to 12 parts of waterborne siloxane, 1 to 3 parts of tartaric acid, 1 to 3 parts of sodium gluconate, 1 to 3 parts of activated silicon dioxide, 1 to 3 parts of volcanic ash, 0.5 to 1.5 parts of bentonite, 0.1 to 0.3 part of a catalyst, 0.1 to 0.3 part of an additive and 32.7 to 42.7 parts of distilled water. The prepared novel environment-friendly permeable crystallization waterproof material is colorless, odorless, non-toxic and harmless like water in appearance, is simple and convenient to construct, only needs to be sprayed on the surface of concrete, then rapidly permeates into the concrete and chemically reacts with calcium ions in cement to generate crystals, the cement and sand are bonded together, and all micropores and capillary channels are blocked to form a waterproof layer with glass density, so that permanent water prevention is realized.
本发明提供了无机水性渗透结晶型防水材料，所述防水材料包括以下重量份原料：硅酸盐25‑35份、碳酸盐8‑12份、火碱1‑3份、活性氧化铝0.5‑1.5份、水性硅氧烷8‑12份、酒石酸1‑3份、葡萄糖酸钠1‑3份、活性二氧化硅1‑3份、火山灰1‑3份、膨润土0.5‑1.5份、催化剂0.1‑0.3份、助剂0.1‑0.3份、蒸馏水32.7‑42.7份。本发明制得的新型环保渗透结晶防水材料，外观像水一样无色无味，无毒无害，而且施工简单方便，只需喷在混凝土表面即可，然后该材料迅速渗透到混凝土内部，与水泥里面的钙离子发生化学反应产生结晶体，把水泥和沙子粘连在一起，堵塞住所有微孔和毛细通道，达到玻璃密度般的防水层，从而实现永久性防水。
Inorganic water-based permeable crystallization waterproof material as well as preparation method and application method thereof
无机水性渗透结晶型防水材料及其制备方法与使用方法
CUI MOHAN (author)
2021-12-07
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
| European Patent Office | 2023
| European Patent Office | 2024
| European Patent Office | 2022
Inorganic-organic composite permeable crystallization type waterproof agent
| European Patent Office | 2015
Film-forming permeable waterproof material, preparation method and application thereof
| European Patent Office | 2020