The invention discloses a preparation method of ceramic Yunlin tea pot. The preparation method comprises the following steps: (1) preparing porcelain clay by taking kaolin as a raw material; (2) making the porcelain making mud into a porcelain blank by using a hand and a throwing tool, and carving and trimming the blank by using a special tool knife, so as to prepare a porcelain jade forest tea soaking blank body capable of being fired; (3) performing low-temperature biscuit firing on the blank body prepared in the step (2) at 900 DEG C; (4) putting the blank obtained after low-temperature firing in the step (3) into a porcelain kiln to be fired at the temperature of 1270 DEG C, and heating for 1-2 hours; (5), maintaining the temperature of the kiln at 1270 DEG C for 40 min, and finally completing kiln burning in the oxidizing atmosphere; (6) naturally cooling the kiln to 60 DEG C for 12 hours, and opening the kiln to obtain a finished product. The ceramic Yunlin tea pot is attractive in style, can be stored for a long time by people, is convenient to preserve and carry, and is longer in collection time and higher in value.
本发明公开了一种瓷玉林茶泡的制备方法，包括以下步骤：1)以高岭土为原料制备制瓷泥；2)将制瓷泥通过用手、拉坯工具制成瓷坯，用专用工具鏨刀完成鏨刻修坯，制备成可以烧制的瓷玉林茶泡胚体；3)将步骤2)做好的胚体进行900℃低温素烧烧制；4)将步骤3)中低温烧制后得到的胚体放入瓷窖中烧制，将窖温烧制1270℃，升温时间1～2小时；然后，窖温保持1270℃，保温40min，最后以氧化气氛结束烧窖；5)窖温进行自然降温，降温至60℃，降温时间为12小时，开窖即可得到成品。本发明得到的陶瓷玉林茶泡样式美观，可供人们长期保存，便于保管携带，收藏时间更长，价值更高。
The invention discloses a preparation method of ceramic Yunlin tea pot. The preparation method comprises the following steps: (1) preparing porcelain clay by taking kaolin as a raw material; (2) making the porcelain making mud into a porcelain blank by using a hand and a throwing tool, and carving and trimming the blank by using a special tool knife, so as to prepare a porcelain jade forest tea soaking blank body capable of being fired; (3) performing low-temperature biscuit firing on the blank body prepared in the step (2) at 900 DEG C; (4) putting the blank obtained after low-temperature firing in the step (3) into a porcelain kiln to be fired at the temperature of 1270 DEG C, and heating for 1-2 hours; (5), maintaining the temperature of the kiln at 1270 DEG C for 40 min, and finally completing kiln burning in the oxidizing atmosphere; (6) naturally cooling the kiln to 60 DEG C for 12 hours, and opening the kiln to obtain a finished product. The ceramic Yunlin tea pot is attractive in style, can be stored for a long time by people, is convenient to preserve and carry, and is longer in collection time and higher in value.
本发明公开了一种瓷玉林茶泡的制备方法，包括以下步骤：1)以高岭土为原料制备制瓷泥；2)将制瓷泥通过用手、拉坯工具制成瓷坯，用专用工具鏨刀完成鏨刻修坯，制备成可以烧制的瓷玉林茶泡胚体；3)将步骤2)做好的胚体进行900℃低温素烧烧制；4)将步骤3)中低温烧制后得到的胚体放入瓷窖中烧制，将窖温烧制1270℃，升温时间1～2小时；然后，窖温保持1270℃，保温40min，最后以氧化气氛结束烧窖；5)窖温进行自然降温，降温至60℃，降温时间为12小时，开窖即可得到成品。本发明得到的陶瓷玉林茶泡样式美观，可供人们长期保存，便于保管携带，收藏时间更长，价值更高。
Geomorphological Analysis and Modelling Studies of Yunlin Coast
| British Library Conference Proceedings | 1997
Land Subsidence Caused by Groundwater Exploitation in Yunlin, Taiwan
| HENRY – Federal Waterways Engineering and Research Institute (BAW) | 2016
Fluctuation of nearshore water quality during a tidal cycle in Yunlin County
| British Library Conference Proceedings | 2005
Modeling Groundwater Flow and Land Subsidence in Yun-Chia Plain and Yunlin Offshore Industrial Area
| British Library Conference Proceedings | 1995