Preparation method and application of ferrite-ceramic heterogeneous co-fired material
The invention discloses a preparation method and application of a ferrite-ceramic heterogeneous co-fired material. The preparation method comprises the following steps: preparing ferrite and ceramic with equivalent sintering temperature and shrinkage rate; ferrite and ceramic are subjected to lamination, lamination and cutting treatment to obtain a ferrite-ceramic heterogeneous co-fired material green body, and then the green body is sintered at the temperature lower than 950 DEG C to obtain a finished product; wherein the ferrite is a Li-series ferrite-sintering aid composite system or a Ni-series ferrite-sintering aid composite system, and the ceramic is a glass-ceramic filler composite system. According to the preparation method, the ferrite and the ceramic can be matched and co-fired at the temperature lower than 950 DEG C, the problem of shrinkage mismatch is avoided, and the prepared co-fired material can be applied to integrated design and manufacturing of X-millimeter wave band circulators and is beneficial to miniaturization development of T/R assemblies.
本发明公开一种铁氧体‑陶瓷异质共烧材料的制备方法及应用,所述制备方法包括如下步骤:制备烧结温度和收缩率相当的铁氧体和陶瓷;将铁氧体和陶瓷经叠片,层压,裁切处理得铁氧体‑陶瓷异质共烧材料生坯料,然后在低于950℃的温度下进行烧结,得到成品;其中,所述铁氧体为Li系铁氧体‑助烧剂复合体系或Ni系铁氧体‑助烧剂复合体系,所述陶瓷为玻璃‑陶瓷填料复合体系。该制备方法可以将铁氧体和陶瓷实现低于950℃下匹配共烧,无收缩率失配问题,并且制备的共烧材料可用于X‑毫米波段环行器的集成化设计与制造中,有利于T/R组件的小型化发展。
Preparation method and application of ferrite-ceramic heterogeneous co-fired material
The invention discloses a preparation method and application of a ferrite-ceramic heterogeneous co-fired material. The preparation method comprises the following steps: preparing ferrite and ceramic with equivalent sintering temperature and shrinkage rate; ferrite and ceramic are subjected to lamination, lamination and cutting treatment to obtain a ferrite-ceramic heterogeneous co-fired material green body, and then the green body is sintered at the temperature lower than 950 DEG C to obtain a finished product; wherein the ferrite is a Li-series ferrite-sintering aid composite system or a Ni-series ferrite-sintering aid composite system, and the ceramic is a glass-ceramic filler composite system. According to the preparation method, the ferrite and the ceramic can be matched and co-fired at the temperature lower than 950 DEG C, the problem of shrinkage mismatch is avoided, and the prepared co-fired material can be applied to integrated design and manufacturing of X-millimeter wave band circulators and is beneficial to miniaturization development of T/R assemblies.
本发明公开一种铁氧体‑陶瓷异质共烧材料的制备方法及应用,所述制备方法包括如下步骤:制备烧结温度和收缩率相当的铁氧体和陶瓷;将铁氧体和陶瓷经叠片,层压,裁切处理得铁氧体‑陶瓷异质共烧材料生坯料,然后在低于950℃的温度下进行烧结,得到成品;其中,所述铁氧体为Li系铁氧体‑助烧剂复合体系或Ni系铁氧体‑助烧剂复合体系,所述陶瓷为玻璃‑陶瓷填料复合体系。该制备方法可以将铁氧体和陶瓷实现低于950℃下匹配共烧,无收缩率失配问题,并且制备的共烧材料可用于X‑毫米波段环行器的集成化设计与制造中,有利于T/R组件的小型化发展。
Preparation method and application of ferrite-ceramic heterogeneous co-fired material
一种铁氧体-陶瓷异质共烧材料的制备方法及应用
CAO DI (author) / YUAN LIXIN (author) / DU ZHAOFU (author) / YAN XU (author)
2022-03-01
Patent
Electronic Resource
Chinese
Preparation method of ferrite embedded dielectric ceramic co-fired substrate
European Patent Office | 2023
|High-temperature fired ferrite-ceramic integrated base plate and preparation method
European Patent Office | 2015
|European Patent Office | 2021
|Barium ferrite ceramic material and preparation method thereof
European Patent Office | 2021
|Low-temperature co-fired ceramic material and preparation method thereof
European Patent Office | 2015
|