Nickel zinc ferrite material and manufacturing method thereof
The invention discloses a nickel zinc ferrite material and a manufacturing method thereof. The nickel-zinc ferrite material comprises a main component, an additive and a glass material, and the main component comprises the following components in percentage by weight: 65 to 66.5 percent of Fe2O3, 9.5 to 11.0 percent of NiO, 19.5 to 21.5 percent of ZnO and 3.4 to 4.6 percent of CuO; the additive is prepared from the following components in percentage by weight: 0.2 to 0.4 percent of Co2O3 and 0.2 to 0.8 percent of frit; the glass frit is prepared from the following components in percentage by weight: 60 percent to 70 percent of Bi2O3, 8 percent to 15 percent of ZnO, 5 percent to 15 percent of B2O3, 1 percent to 5 percent of SiO2 and 1 percent to 2 percent of CuO. According to the invention, the overplating phenomenon can be improved, and the prepared crystal grains are fine and uniform.
本申请公开一种镍锌铁氧体材料及其制造方法。镍锌铁氧体材料包括主成分、添加剂和玻璃料,以重量百分比计算,主成分包括:65wt%~66.5wt%的Fe2O3、9.5wt%~11.0wt%的NiO、19.5wt%~21.5wt%的ZnO、3.4wt%~4.6wt%的CuO;添加剂包括:0.2wt%~0.4wt%的Co2O3、0.2wt%~0.8wt%的玻璃料;以重量百分比计算,玻璃料包括:60wt%~70wt%的Bi2O3、8wt%~15wt%的ZnO、5wt%~15wt%的B2O3、1wt%~5wt%的SiO2、1wt%~2wt%的CuO。本申请可以改善爬镀现象,且制得的晶粒细小均匀。
Nickel zinc ferrite material and manufacturing method thereof
The invention discloses a nickel zinc ferrite material and a manufacturing method thereof. The nickel-zinc ferrite material comprises a main component, an additive and a glass material, and the main component comprises the following components in percentage by weight: 65 to 66.5 percent of Fe2O3, 9.5 to 11.0 percent of NiO, 19.5 to 21.5 percent of ZnO and 3.4 to 4.6 percent of CuO; the additive is prepared from the following components in percentage by weight: 0.2 to 0.4 percent of Co2O3 and 0.2 to 0.8 percent of frit; the glass frit is prepared from the following components in percentage by weight: 60 percent to 70 percent of Bi2O3, 8 percent to 15 percent of ZnO, 5 percent to 15 percent of B2O3, 1 percent to 5 percent of SiO2 and 1 percent to 2 percent of CuO. According to the invention, the overplating phenomenon can be improved, and the prepared crystal grains are fine and uniform.
本申请公开一种镍锌铁氧体材料及其制造方法。镍锌铁氧体材料包括主成分、添加剂和玻璃料,以重量百分比计算,主成分包括:65wt%~66.5wt%的Fe2O3、9.5wt%~11.0wt%的NiO、19.5wt%~21.5wt%的ZnO、3.4wt%~4.6wt%的CuO;添加剂包括:0.2wt%~0.4wt%的Co2O3、0.2wt%~0.8wt%的玻璃料;以重量百分比计算,玻璃料包括:60wt%~70wt%的Bi2O3、8wt%~15wt%的ZnO、5wt%~15wt%的B2O3、1wt%~5wt%的SiO2、1wt%~2wt%的CuO。本申请可以改善爬镀现象,且制得的晶粒细小均匀。
Nickel zinc ferrite material and manufacturing method thereof
镍锌铁氧体材料及其制造方法
GUO HAI (author) / NIE MIN (author) / ZHU YANJUN (author)
2022-03-04
Patent
Electronic Resource
Chinese
Nickel-zinc ferrite material and preparation method thereof
European Patent Office | 2024
|Nickel-zinc ferrite material and preparation method thereof
European Patent Office | 2020
|Nickel-zinc ferrite material and preparation method thereof
European Patent Office | 2015
|Magnetic nickel-zinc ferrite material and preparation method thereof
European Patent Office | 2021
|Granular nickel-zinc ferrite material and preparation method thereof
European Patent Office | 2020
|