Highlight glaze for ancient building porcelain as well as preparation method and application of highlight glaze
The invention relates to highlight glaze for ancient building porcelain as well as a preparation method and application of the highlight glaze. The highlight glaze for the ancient building porcelain comprises the following components in parts by weight: 20-30 parts of potassium feldspar, 10-15 parts of hollow nanoparticles, 8-10 parts of modified glass beads, 15-20 parts of quartz, 3-6 parts of niobium oxide, 6-8 parts of magnesium oxide, 10-12 parts of a binder, 5-8 parts of barium chromate, 18-20 parts of kaolin and 50-60 parts of water. The preparation method of the highlight glaze for ancient building porcelain comprises the following steps: S1, stirring and mixing potassium feldspar, modified glass beads, quartz, niobium oxide, magnesium oxide, barium chromate, kaolin and water, and performing ball milling to obtain glaze slip; s2, stirring and mixing a binder and the hollow nanoparticles; and S3, uniformly mixing the glaze slip obtained in the step S1 and the mixture obtained in the step S2 to obtain the highlight glaze for the ancient building porcelain. The prepared highlight glaze for ancient building porcelain is smooth in glaze surface, and has excellent glossiness and good mechanical properties.
本发明涉及一种古建瓷用高光釉及其制备方法和应用,所述古建瓷用高光釉包括以下重量份的组分:钾长石20‑30份、空心纳米颗粒10‑15份、改性玻璃微珠8‑10份、石英15‑20份、氧化铌3‑6份、氧化镁6‑8份、粘结剂10‑12份、铬酸钡5‑8份、高岭土18‑20份和水50‑60份;所述古建瓷用高光釉的制备方法,包括以下步骤:S1:将钾长石、改性玻璃微珠、石英、氧化铌、氧化镁、铬酸钡、高岭土和水搅拌混合,球磨成釉浆;S2:将粘结剂和空心纳米颗粒搅拌混合;S3:将步骤S1所得釉浆和步骤S2所得混合物混合均匀,即得古建瓷用高光釉。本发明制得的古建瓷用高光釉釉面光滑,且具有优异的光泽度和良好的机械性能。
Highlight glaze for ancient building porcelain as well as preparation method and application of highlight glaze
The invention relates to highlight glaze for ancient building porcelain as well as a preparation method and application of the highlight glaze. The highlight glaze for the ancient building porcelain comprises the following components in parts by weight: 20-30 parts of potassium feldspar, 10-15 parts of hollow nanoparticles, 8-10 parts of modified glass beads, 15-20 parts of quartz, 3-6 parts of niobium oxide, 6-8 parts of magnesium oxide, 10-12 parts of a binder, 5-8 parts of barium chromate, 18-20 parts of kaolin and 50-60 parts of water. The preparation method of the highlight glaze for ancient building porcelain comprises the following steps: S1, stirring and mixing potassium feldspar, modified glass beads, quartz, niobium oxide, magnesium oxide, barium chromate, kaolin and water, and performing ball milling to obtain glaze slip; s2, stirring and mixing a binder and the hollow nanoparticles; and S3, uniformly mixing the glaze slip obtained in the step S1 and the mixture obtained in the step S2 to obtain the highlight glaze for the ancient building porcelain. The prepared highlight glaze for ancient building porcelain is smooth in glaze surface, and has excellent glossiness and good mechanical properties.
本发明涉及一种古建瓷用高光釉及其制备方法和应用,所述古建瓷用高光釉包括以下重量份的组分:钾长石20‑30份、空心纳米颗粒10‑15份、改性玻璃微珠8‑10份、石英15‑20份、氧化铌3‑6份、氧化镁6‑8份、粘结剂10‑12份、铬酸钡5‑8份、高岭土18‑20份和水50‑60份;所述古建瓷用高光釉的制备方法,包括以下步骤:S1:将钾长石、改性玻璃微珠、石英、氧化铌、氧化镁、铬酸钡、高岭土和水搅拌混合,球磨成釉浆;S2:将粘结剂和空心纳米颗粒搅拌混合;S3:将步骤S1所得釉浆和步骤S2所得混合物混合均匀,即得古建瓷用高光釉。本发明制得的古建瓷用高光釉釉面光滑,且具有优异的光泽度和良好的机械性能。
Highlight glaze for ancient building porcelain as well as preparation method and application of highlight glaze
一种古建瓷用高光釉及其制备方法和应用
LIN ZHUTUAN (author)
2022-03-18
Patent
Electronic Resource
Chinese
Sanitary ceramic highlight black glaze and preparation method thereof
European Patent Office | 2024
|European Patent Office | 2024
|Preparation method of wear-resistant glaze daily porcelain glaze
European Patent Office | 2020
|Jun porcelain glaze and preparation method of ornamental stone Jun porcelain glaze painting
European Patent Office | 2022
|European Patent Office | 2024
|