Ceramic glaze suitable for ceramic body with high Yellow River mud content and preparation method of ceramic glaze
The invention relates to the technical field of ceramic glazes, in particular to a ceramic glaze suitable for a ceramic body with high Yellow River mud content and a preparation method of the ceramic glaze. The ceramic glaze comprises 8 wt% of kaolin, 27 wt% of calcined zinc oxide, 22 wt% of quartz, 3 wt% of tremolite and 40 wt% of boron glass powder. The preparation method comprises the following steps: firstly, uniformly mixing the raw materials, adding water, and carrying out ball milling; secondly, drying and ball-milling the glaze slip, and sieving the glaze slip with 250 meshes to obtain dry blank powder; and finally, pressing the dry blank powder into a wafer, drying after glaze dipping, seeding, fully melting, carrying out water quenching and drying to obtain a ceramic frit, and crushing to obtain the ceramic glaze. The ceramic glaze belongs to crystal glaze suitable for ceramic blanks with high Yellow River sludge content, the preparation method replaces a traditional glaze preparation method, the operation mode is simple, the firing process is stable, and the practicability is high.
本发明涉及陶瓷釉料技术领域，特别是涉及一种适用于高黄河泥含量瓷坯的陶瓷釉料及其制备方法。该陶瓷釉料包括：高岭土8wt.％，煅烧氧化锌27wt.％，石英22wt.％，透闪石3wt.％，硼玻璃粉40wt.％；其制备方法包括：首先，将原料混合均匀后加水进行球磨；其次，烘干球磨后釉浆过筛250目得干坯粉料；最后，干坯粉料压制成圆片，浸釉后干燥，点晶种，充分熔融，水淬后烘干，制得陶瓷熔块，粉碎得到陶瓷釉料。该陶瓷釉料属适用于高黄河淤泥含量瓷坯的结晶釉，制备方法替代传统制备釉料的方法，操作方式简单，烧制过程稳定，实用性强。
Ceramic glaze suitable for ceramic body with high Yellow River mud content and preparation method of ceramic glaze
The invention relates to the technical field of ceramic glazes, in particular to a ceramic glaze suitable for a ceramic body with high Yellow River mud content and a preparation method of the ceramic glaze. The ceramic glaze comprises 8 wt% of kaolin, 27 wt% of calcined zinc oxide, 22 wt% of quartz, 3 wt% of tremolite and 40 wt% of boron glass powder. The preparation method comprises the following steps: firstly, uniformly mixing the raw materials, adding water, and carrying out ball milling; secondly, drying and ball-milling the glaze slip, and sieving the glaze slip with 250 meshes to obtain dry blank powder; and finally, pressing the dry blank powder into a wafer, drying after glaze dipping, seeding, fully melting, carrying out water quenching and drying to obtain a ceramic frit, and crushing to obtain the ceramic glaze. The ceramic glaze belongs to crystal glaze suitable for ceramic blanks with high Yellow River sludge content, the preparation method replaces a traditional glaze preparation method, the operation mode is simple, the firing process is stable, and the practicability is high.
本发明涉及陶瓷釉料技术领域，特别是涉及一种适用于高黄河泥含量瓷坯的陶瓷釉料及其制备方法。该陶瓷釉料包括：高岭土8wt.％，煅烧氧化锌27wt.％，石英22wt.％，透闪石3wt.％，硼玻璃粉40wt.％；其制备方法包括：首先，将原料混合均匀后加水进行球磨；其次，烘干球磨后釉浆过筛250目得干坯粉料；最后，干坯粉料压制成圆片，浸釉后干燥，点晶种，充分熔融，水淬后烘干，制得陶瓷熔块，粉碎得到陶瓷釉料。该陶瓷釉料属适用于高黄河淤泥含量瓷坯的结晶釉，制备方法替代传统制备釉料的方法，操作方式简单，烧制过程稳定，实用性强。
Ceramic glaze suitable for ceramic body with high Yellow River mud content and preparation method of ceramic glaze
一种适用于高黄河泥含量瓷坯的陶瓷釉料及其制备方法
FENG SHANXIN (author) / LI XUELIN (author) / ZHANG FENGYI (author) / ZHANG QIANWEN (author)
2023-01-31
Patent
Electronic Resource
Chinese
Transmutation glaze suitable for ceramic tile production and transmutation glaze ceramic tile
| European Patent Office | 2015