Preparation method of powder ceramic
The invention discloses a preparation method of powder ceramic. The preparation method comprises the following steps: step 1, preparing the following raw materials: 15 parts of talcum powder, 0.5 part of sodium silicate, 0.3 part of a sodium hydroxide solution, 50 parts of quartz sand, 25 parts of moonstone powder and 10 parts of silicon dioxide; 2, mixing and grinding the raw materials in the step 1, sieving and storing; step 3, mixing and stirring the sieved powder and deionized water according to a ratio of 1: 45 to prepare coarse slurry; 4, further grinding the coarse slurry in the step 3 to prepare fine slurry; 5, pressing and sintering the fine slurry in the step 4, wherein the sintering temperature is 800-900 DEG C; and step 6, sintering the sintered product again at the sintering temperature of 1000-1200 DEG C for 6-8 hours to obtain a ceramic finished product.
本发明公开了一种粉料陶瓷的制备方法，包括以下步骤：步骤一，准备以下原料：15份滑石粉、0.5份硅酸钠、0.3份氢氧化钠溶液、50份石英砂、25份月长石粉和10份二氧化硅；步骤二，将步骤一中的原料混合磨碎，进行过筛后储存；步骤三，将过筛后的粉料与去离子水按照1：45的比例混合搅拌，制成粗浆料；步骤四，将步骤三中的粗浆料进一步研磨，制成细浆料；步骤五，将步骤四中的细浆料压制并烧结，烧结温度为800‑900℃；步骤六，将烧结后的制品再次烧结，烧结温度为1000‑1200℃，时间6‑8h，制得陶瓷成品。
Preparation method of powder ceramic
The invention discloses a preparation method of powder ceramic. The preparation method comprises the following steps: step 1, preparing the following raw materials: 15 parts of talcum powder, 0.5 part of sodium silicate, 0.3 part of a sodium hydroxide solution, 50 parts of quartz sand, 25 parts of moonstone powder and 10 parts of silicon dioxide; 2, mixing and grinding the raw materials in the step 1, sieving and storing; step 3, mixing and stirring the sieved powder and deionized water according to a ratio of 1: 45 to prepare coarse slurry; 4, further grinding the coarse slurry in the step 3 to prepare fine slurry; 5, pressing and sintering the fine slurry in the step 4, wherein the sintering temperature is 800-900 DEG C; and step 6, sintering the sintered product again at the sintering temperature of 1000-1200 DEG C for 6-8 hours to obtain a ceramic finished product.
本发明公开了一种粉料陶瓷的制备方法，包括以下步骤：步骤一，准备以下原料：15份滑石粉、0.5份硅酸钠、0.3份氢氧化钠溶液、50份石英砂、25份月长石粉和10份二氧化硅；步骤二，将步骤一中的原料混合磨碎，进行过筛后储存；步骤三，将过筛后的粉料与去离子水按照1：45的比例混合搅拌，制成粗浆料；步骤四，将步骤三中的粗浆料进一步研磨，制成细浆料；步骤五，将步骤四中的细浆料压制并烧结，烧结温度为800‑900℃；步骤六，将烧结后的制品再次烧结，烧结温度为1000‑1200℃，时间6‑8h，制得陶瓷成品。
Preparation method of powder ceramic
一种粉料陶瓷的制备方法
ZHANG LINYUE (author) / CAI XILAI (author)
2023-02-21
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Ceramic powder optimization method, ceramic powder preparation method and powder preparation system
| European Patent Office | 2021
Ceramic powder and powder preparation method of ceramic sheet substrate
| European Patent Office | 2024
Preparation method of ceramic powder, ceramic slurry and porous ceramic
| European Patent Office | 2024